Supporting information
Crystallographic Information File (CIF) https://doi.org/10.1107/S1600536803001612/ob6210sup1.cif | |
Structure factor file (CIF format) https://doi.org/10.1107/S1600536803001612/ob6210Isup2.hkl |
CCDC reference: 204716
The title compound, (I), was prepared according to a method described in the literature (Zambounis et al., 1996). The sample was purified by sublimation at about 623 K, using a two zone furnace (Mizuguchi, 1981). Single crystals of (I) were then grown from a solution in dimethylformamide. The present material is quite fragile, so that cutting of the crystal using a safety razor impairs the quality of the crystal. For this reason, we used the single-crystal as grown.
All H atoms were positioned by calculation but were not refined. Special caution was taken to the position of H atoms of the methyl group on the basis of the difference Fourier maps.
Data collection: PROCESS-AUTO (Rigaku, 1998); cell refinement: PROCESS-AUTO; data reduction: TEXSAN (Molecular Structure Corporation, 2001); program(s) used to solve structure: SIR88 (Burla et al., 1989); program(s) used to refine structure: TEXSAN; molecular graphics: ORTEPIII (Burnett & Johnson, 1996); software used to prepare material for publication: TEXSAN.
Fig. 1. A view of the molecular structure of (I), showing 50% displacement ellipsoids for the non-H atoms. |
C22H16N2O2 | F(000) = 356 |
Mr = 340.38 | Dx = 1.444 Mg m−3 |
Monoclinic, P21/c | Mo Kα radiation, λ = 0.7107 Å |
a = 4.928 (3) Å | Cell parameters from 25 reflections |
b = 11.103 (3) Å | θ = 14.7–14.9° |
c = 14.462 (2) Å | µ = 0.09 mm−1 |
β = 98.39 (2)° | T = 223 K |
V = 782.8 (4) Å3 | Platelet, red |
Z = 2 | 1.18 × 0.17 × 0.07 mm |
Rigaku AFC-7R diffractometer | Rint = 0.013 |
ω–2θ scans | θmax = 27.5° |
Absorption correction: ψ scan (North et al., 1968) | h = −6→0 |
Tmin = 0.947, Tmax = 0.998 | k = 0→14 |
2107 measured reflections | l = −18→18 |
1797 independent reflections | 3 standard reflections every 150 reflections |
1349 reflections with F2 > 2σ(F2) | intensity decay: 1.3% |
Refinement on F2 | H-atom parameters not refined |
R[F2 > 2σ(F2)] = 0.044 | w = 1/[σ2(Fo2) + {0.05[Max(Fo2,0) + 2Fc2]/3}2] |
wR(F2) = 0.126 | (Δ/σ)max = 0.001 |
S = 1.59 | Δρmax = 0.21 e Å−3 |
1747 reflections | Δρmin = −0.17 e Å−3 |
118 parameters |
C22H16N2O2 | V = 782.8 (4) Å3 |
Mr = 340.38 | Z = 2 |
Monoclinic, P21/c | Mo Kα radiation |
a = 4.928 (3) Å | µ = 0.09 mm−1 |
b = 11.103 (3) Å | T = 223 K |
c = 14.462 (2) Å | 1.18 × 0.17 × 0.07 mm |
β = 98.39 (2)° |
Rigaku AFC-7R diffractometer | 1349 reflections with F2 > 2σ(F2) |
Absorption correction: ψ scan (North et al., 1968) | Rint = 0.013 |
Tmin = 0.947, Tmax = 0.998 | 3 standard reflections every 150 reflections |
2107 measured reflections | intensity decay: 1.3% |
1797 independent reflections |
R[F2 > 2σ(F2)] = 0.044 | 118 parameters |
wR(F2) = 0.126 | H-atom parameters not refined |
S = 1.59 | Δρmax = 0.21 e Å−3 |
1747 reflections | Δρmin = −0.17 e Å−3 |
Refinement. Refinement using reflections with F2 > −3.0 σ(F2). The weighted R-factor (wR) and goodness of fit (S) are based on F2. R-factor (gt) are based on F. The threshold expression of F2 > 2.0 σ(F2) is used only for calculating R-factor (gt). |
x | y | z | Uiso*/Ueq | ||
O1 | 0.3115 (3) | 0.7365 (1) | −0.12444 (7) | 0.0480 (3) | |
N1 | 0.4143 (2) | 0.58724 (9) | 0.13854 (7) | 0.0237 (2) | |
C1 | 0.7310 (3) | 0.8262 (1) | 0.01053 (10) | 0.0338 (3) | |
C2 | 0.9407 (3) | 0.8648 (1) | 0.0773 (1) | 0.0358 (3) | |
C3 | 0.9722 (3) | 0.8110 (1) | 0.16559 (9) | 0.0317 (3) | |
C4 | 0.7988 (3) | 0.7214 (1) | 0.18705 (8) | 0.0273 (3) | |
C5 | 0.5848 (2) | 0.6794 (1) | 0.11876 (8) | 0.0226 (3) | |
C6 | 0.5536 (2) | 0.7332 (1) | 0.02929 (8) | 0.0260 (3) | |
C7 | 0.3424 (3) | 0.6922 (1) | −0.04536 (9) | 0.0296 (3) | |
C8 | 0.1689 (2) | 0.5933 (1) | −0.02056 (8) | 0.0231 (3) | |
C9 | 0.2095 (2) | 0.5436 (1) | 0.07058 (7) | 0.0217 (3) | |
C10 | 0.0369 (2) | 0.4500 (1) | 0.08876 (8) | 0.0241 (3) | |
C11 | 0.4437 (3) | 0.5355 (1) | 0.23233 (9) | 0.0384 (4) | |
H1 | 0.7050 | 0.8634 | −0.0492 | 0.0405* | |
H2 | 1.0619 | 0.9267 | 0.0637 | 0.0425* | |
H3 | 1.1173 | 0.8367 | 0.2120 | 0.0377* | |
H4 | 0.8226 | 0.6877 | 0.2480 | 0.0327* | |
H5 | 0.0570 | 0.4141 | 0.1491 | 0.0287* | |
H6 | 0.5907 | 0.5734 | 0.2710 | 0.0458* | |
H7 | 0.2784 | 0.5468 | 0.2578 | 0.0458* | |
H8 | 0.4802 | 0.4514 | 0.2289 | 0.0458* |
U11 | U22 | U33 | U12 | U13 | U23 | |
O1 | 0.0575 (7) | 0.0550 (7) | 0.0267 (5) | −0.0296 (6) | −0.0096 (4) | 0.0124 (5) |
N1 | 0.0256 (5) | 0.0249 (5) | 0.0189 (4) | −0.0038 (4) | −0.0025 (3) | −0.0004 (4) |
C1 | 0.0369 (7) | 0.0327 (7) | 0.0303 (6) | −0.0106 (5) | −0.0002 (5) | 0.0024 (5) |
C2 | 0.0362 (7) | 0.0331 (7) | 0.0368 (7) | −0.0132 (5) | 0.0006 (5) | −0.0028 (5) |
C3 | 0.0291 (6) | 0.0320 (6) | 0.0319 (6) | −0.0067 (5) | −0.0020 (5) | −0.0083 (5) |
C4 | 0.0268 (6) | 0.0290 (6) | 0.0245 (5) | −0.0020 (4) | −0.0019 (4) | −0.0054 (4) |
C5 | 0.0220 (5) | 0.0218 (5) | 0.0230 (5) | −0.0002 (4) | −0.0003 (4) | −0.0040 (4) |
C6 | 0.0270 (6) | 0.0261 (6) | 0.0238 (5) | −0.0046 (5) | 0.0000 (4) | −0.0011 (4) |
C7 | 0.0318 (6) | 0.0324 (6) | 0.0233 (5) | −0.0088 (5) | −0.0008 (5) | 0.0019 (5) |
C8 | 0.0238 (5) | 0.0243 (5) | 0.0204 (5) | −0.0027 (4) | 0.0008 (4) | −0.0015 (4) |
C9 | 0.0220 (5) | 0.0222 (5) | 0.0197 (5) | −0.0001 (4) | −0.0012 (4) | −0.0030 (4) |
C10 | 0.0255 (5) | 0.0260 (6) | 0.0197 (5) | −0.0023 (4) | −0.0008 (4) | −0.0003 (4) |
C11 | 0.0460 (8) | 0.0417 (8) | 0.0231 (6) | −0.0140 (6) | −0.0092 (5) | 0.0060 (5) |
O1—C7 | 1.234 (2) | C4—H4 | 0.949 |
N1—C5 | 1.380 (2) | C5—C6 | 1.413 (2) |
N1—C9 | 1.389 (1) | C6—C7 | 1.459 (2) |
N1—C11 | 1.461 (2) | C7—C8 | 1.468 (2) |
C1—C2 | 1.376 (2) | C8—C9 | 1.416 (2) |
C1—C6 | 1.405 (2) | C8—C10i | 1.393 (2) |
C1—H1 | 0.950 | C9—C10 | 1.392 (2) |
C2—C3 | 1.398 (2) | C10—H5 | 0.951 |
C2—H2 | 0.949 | C11—H6 | 0.947 |
C3—C4 | 1.376 (2) | C11—H7 | 0.950 |
C3—H3 | 0.950 | C11—H8 | 0.953 |
C4—C5 | 1.414 (2) | ||
O1···C3ii | 3.288 (2) | C2···C8vi | 3.581 (2) |
O1···C11iii | 3.394 (2) | C3···C5vi | 3.507 (2) |
O1···C4ii | 3.468 (2) | C3···C9vi | 3.541 (2) |
N1···C3iv | 3.364 (2) | C4···C9vi | 3.439 (2) |
N1···C8v | 3.489 (2) | C5···C10vi | 3.453 (2) |
N1···C4iv | 3.540 (2) | C5···C9vi | 3.587 (2) |
N1···C10vi | 3.592 (2) | C6···C10v | 3.482 (2) |
C1···C8vi | 3.439 (2) | C6···C8vi | 3.572 (2) |
C1···C7vi | 3.557 (2) | C7···C9v | 3.478 (2) |
C2···C7vi | 3.430 (2) | C7···C10v | 3.578 (2) |
C2···C6vi | 3.515 (2) | C8···C9v | 3.586 (2) |
C5—N1—C9 | 120.89 (10) | C5—C6—C7 | 121.1 (1) |
C5—N1—C11 | 120.21 (10) | O1—C7—C6 | 122.7 (1) |
C9—N1—C11 | 118.9 (1) | O1—C7—C8 | 121.8 (1) |
C2—C1—C6 | 121.2 (1) | C6—C7—C8 | 115.5 (1) |
C2—C1—H1 | 119.4 | C7—C8—C9 | 120.7 (1) |
C6—C1—H1 | 119.4 | C7—C8—C10i | 118.3 (1) |
C1—C2—C3 | 118.7 (1) | C9—C8—C10i | 120.9 (1) |
C1—C2—H2 | 120.8 | N1—C9—C8 | 120.8 (1) |
C3—C2—H2 | 120.6 | N1—C9—C10 | 121.9 (1) |
C2—C3—C4 | 121.7 (1) | C8—C9—C10 | 117.4 (1) |
C2—C3—H3 | 119.2 | C8i—C10—C9 | 121.7 (1) |
C4—C3—H3 | 119.1 | C8i—C10—H5 | 118.2 |
C3—C4—C5 | 120.3 (1) | C9—C10—H5 | 120.1 |
C3—C4—H4 | 119.8 | N1—C11—H6 | 109.7 |
C5—C4—H4 | 119.8 | N1—C11—H7 | 109.5 |
N1—C5—C4 | 120.9 (1) | N1—C11—H8 | 109.3 |
N1—C5—C6 | 120.98 (10) | H6—C11—H7 | 109.7 |
C4—C5—C6 | 118.1 (1) | H6—C11—H8 | 109.4 |
C1—C6—C5 | 120.0 (1) | H7—C11—H8 | 109.2 |
C1—C6—C7 | 118.9 (1) |
Symmetry codes: (i) −x, −y+1, −z; (ii) x−1, −y+3/2, z−1/2; (iii) x, −y+3/2, z−1/2; (iv) x−1, y, z; (v) −x+1, −y+1, −z; (vi) x+1, y, z. |
Experimental details
Crystal data | |
Chemical formula | C22H16N2O2 |
Mr | 340.38 |
Crystal system, space group | Monoclinic, P21/c |
Temperature (K) | 223 |
a, b, c (Å) | 4.928 (3), 11.103 (3), 14.462 (2) |
β (°) | 98.39 (2) |
V (Å3) | 782.8 (4) |
Z | 2 |
Radiation type | Mo Kα |
µ (mm−1) | 0.09 |
Crystal size (mm) | 1.18 × 0.17 × 0.07 |
Data collection | |
Diffractometer | Rigaku AFC-7R diffractometer |
Absorption correction | ψ scan (North et al., 1968) |
Tmin, Tmax | 0.947, 0.998 |
No. of measured, independent and observed [F2 > 2σ(F2)] reflections | 2107, 1797, 1349 |
Rint | 0.013 |
(sin θ/λ)max (Å−1) | 0.649 |
Refinement | |
R[F2 > 2σ(F2)], wR(F2), S | 0.044, 0.126, 1.59 |
No. of reflections | 1747 |
No. of parameters | 118 |
No. of restraints | ? |
H-atom treatment | H-atom parameters not refined |
Δρmax, Δρmin (e Å−3) | 0.21, −0.17 |
Computer programs: PROCESS-AUTO (Rigaku, 1998), PROCESS-AUTO, TEXSAN (Molecular Structure Corporation, 2001), SIR88 (Burla et al., 1989), TEXSAN, ORTEPIII (Burnett & Johnson, 1996).
O1—C7 | 1.234 (2) | C4—C5 | 1.414 (2) |
N1—C5 | 1.380 (2) | C5—C6 | 1.413 (2) |
N1—C9 | 1.389 (1) | C6—C7 | 1.459 (2) |
N1—C11 | 1.461 (2) | C7—C8 | 1.468 (2) |
C1—C2 | 1.376 (2) | C8—C9 | 1.416 (2) |
C1—C6 | 1.405 (2) | C8—C10i | 1.393 (2) |
C2—C3 | 1.398 (2) | C9—C10 | 1.392 (2) |
C3—C4 | 1.376 (2) |
Symmetry code: (i) −x, −y+1, −z. |
The crystal structure of the title compound, (I), was reported not only by Zavodnik et al. (1981) but also by Ohmasa & Susse (1976). The present paper provides some additional results at 223 K with higher precision. We have been conducting a series of investigations on the correlation between the color in the solid state and crystal structures in quinacridone pigments. Special attention has been focused on the effect of N—H···O intermolecular hydrogen bonds on the color as well as on the stability of the compounds. For this reason, we have tackled three representative quinacridone compounds with various hydrogen bonds, namely unsubstituted quinacridone with two NH groups (four hydrogen bonds per molecule; Mizuguchi, Sasaki & Tojo, 2002), the monomethyl derivative with one NH group (two hydrogen bonds per molecule; Zambounis & Mizuguchi, 1996; Mizuguchi & Senju, 2002) and the dimethyl derivative with no NH group (i.e. the title compound; no hydrogen bonds per molecule). Compound (I) has also recently attracted attention as a doping material for electroluminescence applications (Shi & Tang, 1997). In this connection, the present reinvestigation has been carried out.
Our results are basically in good agreement with those of Zavodnik et al. (1981). The molecule is entirely planar, as shown in Fig. 1, and belongs to the point group of Ci. The molecules are stacked with major overlap of the acridine skeleton along the a axis. Our result is Rgt = 0.044 for 1747 reflections (reflection/parameter ratio = 14.8), while R = 0.047 for 532 reflections with I greater than 3σ in Zavodnik's study. Since the measurement temperatures were different (at 223 K in our case but room temperature in Zavodnik's study), direct comparison of the structural parameters seems rather difficult. However, the s.u. values of the bond parameters have been improved significantly in the present investigation: the values in (I) are 0.002 Å for the bond lengths C—C, C—N and C—O, whereas the values were in the range 0.005–0.007 Å in Zavodnik's study. As for the bond angles C—C—C, C—C—N, C—N—C and C—C—O, our s.u. values are 0.1°, while a range of 0.4–0.6° was reported for Zavodnik's study. Our results also include displacement displacement parameters for non-H atoms.