Topology and temperature dependence of the diffuse X-ray scattering in Na0.5Bi0.5TiO3 ferroelectric single crystals

CROSSMARK_Color_square_no_text.svg

aDepartment of Physics, University of Siegen, Walter-Flex Strasse 3, Siegen 57072, Germany, bDiamond Light Source, Harwell Science and Innovation Campus, Didcot OX11 0DE, UK, and cDepartment of Physics, University of Warwick, Gibbet Hill Road, Coventry CV4 7AL, UK
*Correspondence e-mail: gorfman@physik.uni-siegen.de

Edited by G. Kostorz, ETH Zurich, Switzerland (Received 29 April 2015; accepted 21 August 2015; online 20 September 2015)

The results of high-resolution measurements of the diffuse X-ray scattering produced by a perovskite-based Na0.5Bi0.5TiO3 ferroelectric single crystal between 40 and 620 K are reported. The study was designed as an attempt to resolve numerous controversies regarding the average structure of Na0.5Bi0.5TiO3, such as the mechanism of the phase transitions between the tetragonal, P4bm, and rhombohedral | monoclinic, R3c | Cc, space groups and the correlation between structural changes and macroscopic physical properties. The starting point was to search for any transformations of structural disorder in the temperature range of thermal depoling (420–480 K), where the average structure is known to remain unchanged. The intensity distribution around the {032} pseudocubic reflection was collected using a PILATUS 100K detector at the I16 beamline of the Diamond Light Source (UK). The data revealed previously unknown features of the diffuse scattering, including a system of dual asymmetric L-shaped diffuse scattering streaks. The topology, temperature dependence, and relationship between Bragg and diffuse intensities suggest the presence of complex microstructure in the low-temperature R3c | Cc phase. This microstructure may be formed by the persistence of the higher-temperature P4bm phase, built into a lower-temperature R3c | Cc matrix, accompanied by the related long-range strain fields. Finally, it is shown that a correlation between the temperature dependence of the X-ray scattering features and the temperature regime of thermal depoling is present.

1. Introduction

Na0.5Bi0.5TiO3 (NBT) is a ferroelectric material that is interesting both as the foundation of many potential lead-free piezoelectrics (Takenaka et al., 2008[Takenaka, T., Nagata, H. & Hiruma, Y. (2008). Jpn. J. Appl. Phys. 47, 3787-3801.]) and as a model system for the crystallography of perovskites (Mitchell, 2003[Mitchell, R. H. (2003). Perovskites: Modern and Ancient. Thunder Bay: Almaz-Press.]). NBT is unusual in showing at least two polymorphic structural phase transformations (Vakhrushev et al., 1985[Vakhrushev, S. B., Isupov, V., Kvyatkovsky, B. E., Okuneva, N. M., Pronin, I. P., Smolensky, G. A. & Syrnikov, P. P. (1985). Ferroelectrics, 63, 153-160.]; Park et al., 1996[Park, S. E., Chung, S. J. & Kim, I. T. (1996). J. Am. Ceram. Soc. 79, 1290-1296.]; Jones & Thomas, 2002[Jones, G. O. & Thomas, P. A. (2002). Acta Cryst. B58, 168-178.]), formation of hierarchical domain systems and peculiar structural disorder (Yao et al., 2010[Yao, J., Ge, W., Luo, L., Li, J., Viehland, D. & Luo, H. (2010). Appl. Phys. Lett. 96, 222905.]; Levin & Reaney, 2012[Levin, I. & Reaney, I. M. (2012). Adv. Funct. Mater. 22, 3445-3452.]). Despite a significant number of X-ray and neutron diffraction studies (Jones & Thomas, 2000[Jones, G. O. & Thomas, P. A. (2000). Acta Cryst. B56, 426-430.]; Jones & Thomas, 2002[Jones, G. O. & Thomas, P. A. (2002). Acta Cryst. B58, 168-178.]; Aksel, Forrester, Kowalski et al., 2011[Aksel, E., Forrester, J. S., Kowalski, B., Jones, J. L. & Thomas, P. A. (2011). Appl. Phys. Lett. 99, 222901.]; Ge et al., 2013[Ge, W., Devreugd, C. P., Phelan, D., Zhang, Q., Ahart, M., Li, J., Luo, H., Boatner, L. A., Viehland, D. & Gehring, P. M. (2013). Phys. Rev. B, 88, 174115.]; Rao, Fitch & Ranjan, 2013[Rao, B. N., Fitch, A. & Ranjan, R. (2013). Phys. Rev. B, 87, 060102.]; Rao, Datta et al., 2013[Rao, B. N., Datta, R., Chandrashekaran, S., Mishra, D. K., Sathe, V., Senyshyn, A. & Ranjan, R. (2013). Phys. Rev. B, 88, 224103.]; Carter et al., 2014[Carter, J., Aksel, E., Iamsasri, T., Forrester, J. S., Chen, J. & Jones, J. L. (2014). Appl. Phys. Lett. 104, 112904.]), electron microscopy investigations (Beanland & Thomas, 2011[Beanland, R. & Thomas, P. A. (2011). Scr. Mater. 65, 440-443.]; Dorcet & Trolliard, 2008[Dorcet, V. & Trolliard, G. (2008). Acta Mater. 56, 1753-1761.]; Dorcet et al., 2008[Dorcet, V., Trolliard, G. & Boullay, P. (2008). Chem. Mater. 20, 5061-5073.]; Liu et al., 2012[Liu, Y., Withers, R. L., Wang, J., Norén, L., Studer, A. J. & Li, Y. (2012). J. Adv. Dielect. 02, 1230012.]; Ma et al., 2013[Ma, C., Guo, H. & Tan, X. (2013). Adv. Funct. Mater. 23, 5261-5266.]) and density functional theory calculations (Gröting et al., 2011[Gröting, M., Hayn, S. & Albe, K. (2011). J. Solid State Chem. 184, 2041-2046.], 2012[Gröting, M., Kornev, I., Dkhil, B. & Albe, K. (2012). Phys. Rev. B, 86, 134118.]; Meyer et al., 2015[Meyer, K.-C., Gröting, M. & Albe, K. (2015). J. Solid State Chem. 227, 117-122.]), considerable disagreement about the average structure of NBT remains.

The commonly accepted reference point stems from the seminal neutron powder diffraction study of Jones & Thomas (2002[Jones, G. O. & Thomas, P. A. (2002). Acta Cryst. B58, 168-178.]). They reported two temperature-induced phase transitions, involving changes of average symmetry, realignment of polarization and the modification of oxygen octahedral tilt systems: (a) T ≃ 840 K, the transition between the cubic paraelectric, [Pm\bar 3m], phase and tetragonal ferro(i)electric, P4bm, phase with the a0a0c+ octahedral tilt system according to the Glazer (1972[Glazer, A. M. (1972). Acta Cryst. B28, 3384-3392.]) notation; (b) T ≃ 570 K, the transition between tetragonal ferro(i)electric, P4bm, and rhombohedral ferroelectric, R3c, phases ( a- a- a- octahedral tilt system). Despite the wide acceptance of this phase pattern as a framework, the fine structural details, especially those in the nominally rhombohedral R3c phase, are still the matter of revisions and apparent contradictions. Even the original work of Jones & Thomas (2002[Jones, G. O. & Thomas, P. A. (2002). Acta Cryst. B58, 168-178.]) documented local departures from the R3c average structure in the form of significant disorder of the Bi positions. Furthermore, the mechanism of transition between the structures described by the R3c and P4bm space groups, which lack a group–subgroup relation, remains unexplained.

A rapid reassessment of the NBT average structure began from the single-crystal X-ray diffraction work of Gorfman & Thomas (2010[Gorfman, S. & Thomas, P. A. (2010). J. Appl. Cryst. 43, 1409-1414.]) and synchrotron X-ray powder diffraction work of Aksel, Forrester, Jones et al. (2011[Aksel, E., Forrester, J. S., Jones, J. L., Thomas, P. A., Page, K. & Suchomel, M. R. (2011). Appl. Phys. Lett. 98, 152901.]). Benefiting from the capabilities of modern instruments, both studies independently presented evidence of a lower-symmetry long-range monoclinic phase, with Cc rather than R3c symmetry. Subsequently, Ma et al. (2013[Ma, C., Guo, H. & Tan, X. (2013). Adv. Funct. Mater. 23, 5261-5266.]) have confirmed the long-range Cc symmetry of NBT by careful analysis of the half-integer pseudocubic reflections, using transmission electron microscopy. They noted, however, that the NBT structure evolves into R3c after a small addition of BaTiO3. Rao & Ranjan (2012[Rao, B. N. & Ranjan, R. (2012). Phys. Rev. B, 86, 134103.]) and Rao, Fitch & Ranjan (2013[Rao, B. N., Fitch, A. & Ranjan, R. (2013). Phys. Rev. B, 87, 060102.]) suggested a coexistence of monoclinic and rhombohedral phases below ∼570 K and reported that the monoclinic phase, Cc, can be irreversibly driven into the rhombohedral R3c phase by the application of an external electric field. Observation of optical birefringence in NBT single crystals by Gorfman et al. (2012[Gorfman, S., Glazer, A. M., Noguchi, Y., Miyayama, M., Luo, H. & Thomas, P. A. (2012). J. Appl. Cryst. 45, 444-452.]) supplied further evidence of the monoclinic symmetry of the lower-temperature NBT phase. This work reported a ∼2 (1) K temperature window of optically isotropic phase just below the phase transition at 573 (20) K, which remains unexplained and suggests hidden and complex mechanisms driving this phase transition. However, Beanland & Thomas (2014[Beanland, R. & Thomas, P. A. (2014). Phys. Rev. B, 89, 174102.]) have carefully inspected NBT using a novel computer-controlled electron microscopy technique and concluded that any defect-free areas of NBT must be described by the R3c symmetry. The apparent bulk monoclinic symmetry of NBT was questioned by Ge et al. (2013[Ge, W., Devreugd, C. P., Phelan, D., Zhang, Q., Ahart, M., Li, J., Luo, H., Boatner, L. A., Viehland, D. & Gehring, P. M. (2013). Phys. Rev. B, 88, 174115.]), who suggested that it must be rather attributed to a skin effect. Considering all the existing controversies we will refer to the low-temperature phase here as [R3c \mid Cc].

Another puzzling problem is the mismatch between the reported temperature dependence of the average structure and physical properties: the piezoelectricity in poled NBT ceramics is irreversibly lost upon heating at ∼420–480 K (Hiruma et al., 2009[Hiruma, Y., Nagata, H. & Takenaka, T. (2009). J. Appl. Phys. 105, 084112.]; Aksel et al., 2012[Aksel, E., Forrester, J. S., Kowalski, B., Deluca, M., Damjanovic, D. & Jones, J. L. (2012). Phys. Rev. B, 85, 024121.]; Foronda et al., 2014[Foronda, H., Deluca, M., Aksel, E., Forrester, J. S. & Jones, J. L. (2014). Mater. Lett. 115, 132-135.]). None of the studies report any abrupt structural changes at these temperatures. Only recently, Rao, Datta et al. (2013[Rao, B. N., Datta, R., Chandrashekaran, S., Mishra, D. K., Sathe, V., Senyshyn, A. & Ranjan, R. (2013). Phys. Rev. B, 88, 224103.]) performed temperature-dependent neutron powder diffraction on poled NBT ceramics and suggested that the onset of thermal depoling might be caused by the appearance of regions with octahedral tilt systems matching that of the tetragonal symmetry, P4bm. Thus, the properties of NBT might be influenced by the local structural disorder and microstructure: the parameters which go beyond the average atomic structure.

Indeed, NBT is known for a significant structural disorder. For example, the shortest Bi—O bond distance, calculated from the average structure as 2.53 Å, disagrees with the 2.2 Å bonds observed with EXAFS (Shuvaeva et al., 2005[Shuvaeva, V. A., Zekria, D., Glazer, A. M., Jiang, Q., Weber, S. M., Bhattacharya, P. & Thomas, P. A. (2005). Phys. Rev. B, 71, 174114.]). Keeble et al. (2013[Keeble, D. S., Barney, E. R., Keen, D. A., Tucker, M. G., Kreisel, J. & Thomas, P. A. (2013). Adv. Funct. Mater. 23, 185-190.]) and Aksel et al. (2013[Aksel, E., Forrester, J. S., Nino, J. C., Page, K., Shoemaker, D. P. & Jones, J. L. (2013). Phys. Rev. B, 87, 104113.]) analysed the total neutron scattering by means of reverse Monte Carlo simulation, concluding that accounting for total neutron scattering instead of isolated Bragg peaks resolves this controversy. Further direct evidence of structural disorder is provided by single-crystal diffuse X-ray scattering (DS) (Kreisel et al., 2003[Kreisel, J., Bouvier, P., Dkhil, B., Thomas, P. A., Glazer, A. M., Welberry, T., Chaabane, B. & Mezouar, M. (2003). Phys. Rev. B, 68, 014113.]; Thomas et al., 2010[Thomas, P. A., Trujillo, S., Boudard, M., Gorfman, S. & Kreisel, J. (2010). Solid State Sci. 12, 311-317.]) and singe-crystal neutron scattering data (Balagurov et al., 2006[Balagurov, A. M., Koroleva, E. Y., Naberezhnov, A. A., Sakhnenko, V. P., Savenko, B. N., Ter-Oganessian, N. V. & Vakhrushev, S. B. (2006). Phase Transitions, 79, 163-173.]; Ge et al., 2013[Ge, W., Devreugd, C. P., Phelan, D., Zhang, Q., Ahart, M., Li, J., Luo, H., Boatner, L. A., Viehland, D. & Gehring, P. M. (2013). Phys. Rev. B, 88, 174115.]). Although strong DS is quite common for perovskite-based ferroelectrics and relaxor ferroelectric single crystals (e.g. Xu et al., 2006[Xu, G., Zhong, Z., Bing, Y., Ye, Z.-G. & Shirane, G. (2006). Nat. Mater. 5, 134-140.]; Stock et al., 2007[Stock, C., Xu, G., Gehring, P. M., Luo, H., Zhao, X., Cao, H., Li, J. F., Viehland, D. & Shirane, G. (2007). Phys. Rev. B, 76, 064122.]; Paściak et al., 2012[Paściak, M., Heerdegen, A., Goossens, D. J., Whitfield, R. E., Pietraszko, A. & Welberry, T. R. (2012). Met. Mater. Trans. A, 44, 87-93.]; Bosak et al., 2012[Bosak, A., Chernyshov, D., Vakhrushev, S. & Krisch, M. (2012). Acta Cryst. A68, 117-123.]), X-ray DS in NBT is highly unusual. It exhibits a scheme of asymmetric DS streaks, emanating from the Bragg peaks and generally extending along the lower-angular [\langle 001\rangle^*] directions (the pseudocubic cell setting is used for indexing throughout this study). More specifically, { hkl} reflections ([h, k, l \ne 0]) are decorated by three DS streaks, extending towards decreasing absolute values of |h|, |k| and |l|; { hk0 } reflections ([h, k\ne 0)] are decorated by four streaks: one each extending towards decreasing |h| and |k|, and two others extending towards increasing |l|; { h00 } reflections (h ≠ 0) are decorated by four DS streaks towards increasing |k| and |l|. The intensity of these streaks is hkl dependent: for example, they are particularly strong around {032}-type peaks and can be easily observed using a laboratory-based single-crystal X-ray diffractometer, whereas they are barely visible around e.g. {110}-type peaks. Fig. 1[link] shows (a) typical diffraction data as observed using a laboratory diffractometer, along with (b) a schematic of the DS in the 0kl plane and (c) a schematic of the DS distribution around the [032]* reciprocal lattice point, highlighting the asymmetry of the DS. Kreisel et al. (2003[Kreisel, J., Bouvier, P., Dkhil, B., Thomas, P. A., Glazer, A. M., Welberry, T., Chaabane, B. & Mezouar, M. (2003). Phys. Rev. B, 68, 014113.]) modelled this DS by including planar `island' sheets in the rhombohedral `matrix' of NBT, where Bi and Na atoms are displaced in [\langle{001}\rangle] directions off the threefold 〈111〉 axis. Although this model predicts the appearance of asymmetric DS streaks, it fails to reproduce the exact topology observed, e.g. the presence of local intensity maxima along the streaks (Thomas et al., 2010[Thomas, P. A., Trujillo, S., Boudard, M., Gorfman, S. & Kreisel, J. (2010). Solid State Sci. 12, 311-317.]). It is also only an empirical model and therefore contains no intrinsic chemical or physical reasoning for the formation of such planar sheets. Furthermore, it is not known how the DS changes with temperature and, in contrast to the average structure, whether or not there is evidence in the DS of a structural transition that accompanies the loss of piezoelectric properties at 420–480 K. Finally, Ge et al. (2013[Ge, W., Devreugd, C. P., Phelan, D., Zhang, Q., Ahart, M., Li, J., Luo, H., Boatner, L. A., Viehland, D. & Gehring, P. M. (2013). Phys. Rev. B, 88, 174115.]) reported that neutron diffuse scattering is qualitatively different from X-ray diffuse scattering: while weak [\langle 001\rangle_{}^*]-oriented streaks are observed using neutron scattering, their distribution around Bragg peaks exhibits twofold rotational symmetry.

[Figure 1]
Figure 1
An overview of the previously known information about the topology of the L-shaped DS streaks in NBT. (a) 0kl section of reciprocal space reconstructed from the data collected using a home-laboratory Gemini R diffractometer. (b) A schematic diagram showing the topology of the diffuse scattering streaks (blue) in relation to the Bragg scattering (black). (c) An enlarged three-dimensional schematic view of a smaller reciprocal space volume. The streaks extend along one of the [\langle 001\rangle_{}^*] reciprocal lattice directions.

The first aim of this work is to reinvestigate the exact topology of the X-ray DS by using a state-of-the-art high-resolution synchrotron X-ray diffractometer. The second aim is to probe the temperature dependence of this DS to assess the role of the structural disorder in the physical properties of NBT. Finally, we examine the role of structural disorder in the mechanism of the phase transition between the [R3c \mid Cc] and P4bm phases. Understanding this mechanism in NBT may advance the understanding of structural mechanisms of phase transition in other functional ferroelectrics such as lead zirconate titanate (PbZr1−xTixO3), as well as popular solid solutions of NBT such as Na0.5Bi0.5TiO3–BaTiO3 (NBT–BT).

2. Experiment

High-resolution measurements of the X-ray diffuse scattering were performed at the I16 beamline at Diamond Light Source, UK. An NBT single crystal was grown by the flux method as previously described by Jones & Thomas (2000[Jones, G. O. & Thomas, P. A. (2000). Acta Cryst. B56, 426-430.]). A fragment of straw-coloured crystal was selected, oriented and cut parallel to one of the pseudo-cubically equivalent (011) Miller planes. The crystal of approximately 1 × 1 × 0.1 mm was attached to a silicon wafer using conductive silver paint and then mounted in a Lakeshore cryofurnace. The orientation of the crystal on the silicon wafer ensured easy access to one of the {032} reflections on the I16 six-circle diffractometer. We collected reciprocal space volumes around the [032]* point of reciprocal space and in the temperature range 40–620 K (i.e. up to and beyond the transition to the tetragonal phase at 573 (20) K (Gorfman et al., 2012[Gorfman, S., Glazer, A. M., Noguchi, Y., Miyayama, M., Luo, H. & Thomas, P. A. (2012). J. Appl. Cryst. 45, 444-452.]) on both heating and cooling. The maps were taken every 20 K below 400 K, every 5 K between 400 and 560 K, and every 1 K above 560 K. We tuned the X-ray wavelength/energy to 0.93 Å/13.3 keV: this is close to the Bi LIII absorption edge (0.92 Å/13.4 keV) to balance reciprocal space resolution and attenuation. At this energy and for the geometry of the 032 reflection, the average X-ray penetration depth was 19.7 µm. The scattered intensity in each slice of reciprocal space was measured using a PILATUS 100K detector (DECTRIS), and a reciprocal space volume was built up by taking sequential frames every 0.02° in ω. The resolution in 2θ and χ was set by the pixel size of the PILATUS to ∼0.015°. This experimental methodology resulted in sampling reciprocal space with a resolution of ∼0.0015 pseudocubic reciprocal lattice units (r.l.u.). Furthermore, we benefited from the high dynamic range of the PILATUS (Kraft et al., 2009[Kraft, P., Bergamaschi, A., Broennimann, Ch., Dinapoli, R., Eikenberry, E. F., Henrich, B., Johnson, I., Mozzanica, A., Schlepütz, C. M., Willmott, P. R. & Schmitt, B. (2009). J. Synchrotron Rad. 16, 368-375.]) to capture the intensity extending over strong Bragg and weak diffuse scattering signal.

3. Results

3.1. Topology of the L-shaped diffuse scattering

Fig. 2[link] shows the reconstructed three-dimensional reciprocal space volume (RSV), with isosurfaces of three-dimensional scattering intensity distribution, [I({\bf H})], around the [{{\bf H}_0} = { [{032} ]^*}] reciprocal lattice point, collected at a temperature of 40 K. Fig. 2[link](a) compares the schematics of the RSV from the previous lower-resolution experiments with the result of the presented high-resolution experiments. Figs. 2[link](b) and 2[link](c) view the RSV along the [100]* and [001]* directions, respectively. The detailed RSV (in animated form) is available in the supporting information.

[Figure 2]
Figure 2
Three-dimensional reconstructions of the DS around the [{{\bf H}_0} = { [{032} ]^*}] point of the reciprocal lattice. (a) represents the schematic view of the DS scattering around this point of the reciprocal lattice and reconstructs the three-dimensional contour of the present high-resolution I16 DS measurement. (b), (c) represent the same contours, using different projections. An animated three-dimensional version of this reciprocal space volume is available in the supporting information.

The collection of high-resolution RSVs gives us the added ability to extract reciprocal space maps (RSMs) from arbitrary planes, two of which are shown in Fig. 3[link]. These RSMs highlight the fine details of the DS topology: they pass through the maximum of the three-dimensional scattering intensity and are parallel to the 0kl (Fig. 3[link]a) and h0lr (Fig. 3[link]b) reciprocal space planes, where [ {l}_{\rm r} = {{({\bf H}\cdot {{\bf H}}_{0})}/{{H}_{0}}}], i.e. the projection along the line connecting the origin of reciprocal space to the H0 = [032]* reciprocal lattice point. These RSMs reveal previously unseen features of the DS, which are described below.

[Figure 3]
Figure 3
The crystallographic orientation of the observed DS. (a) A section parallel to 0kl in the crystallographic reference frame in which the data were collected. The arrows indicate the radial ( [032 ]*) and transverse ([{ [{02\bar 3} ]^*}]) crystallographic directions. (b) The h0lr plane, where lr is the projection of the scattering vector onto the [032 ]* direction. The plane is perpendicular to the [{ [{02\bar 3} ]^*}] direction. Both orientations highlight the low-intensity plane appearing perpendicular to the [032 ]* direction. Such low-intensity planes are a typical feature of Huang scattering: diffuse X-ray scattering due to the presence of long-range deformation fields, centred by point defects.
3.1.1. DS Streaks

There are two `systems' of [\langle 001\rangle ^*] DS streaks: stronger streaks extend towards the lower scattering angles (larger d spacing), whilst weaker streaks extend towards the higher scattering angles (smaller d spacing). The stronger streaks were observed in all the previous measurements (Fig. 1[link]). However, this is the first observation of the weaker streaks, which have never been accounted for in any model describing structural disorder in perovskite-based materials.

3.1.2. Bragg peaks

The Bragg peak is split into two components: a stronger component (later referred to as the `matrix' peak) and a second peak of weaker intensity closer to the origin (later referred to as the `island' peak), separated from the stronger component by a plane of low intensity. Careful inspection of the temperature dependence of these peaks will suggest that their splitting cannot be accounted for by twinning/ferroelastic domains.

3.1.3. Relationship between the diffuse scattering streaks and the Bragg peaks

We see that the stronger DS streaks decorate the `island' peak, whilst the weaker DS streaks decorate the `matrix' peak. The two `Bragg' peaks are separated by a plane of low-intensity scattering, which appears perpendicular to the [032]* reciprocal lattice direction. This feature is reminiscent of the plane of low intensity that results from so-called Huang scattering (Ekstein, 1945[Ekstein, H. (1945). Phys. Rev. 68, 120-124.]; Krivoglaz, 1996[Krivoglaz, M. A. (1996). X-ray and Neutron Diffraction in Nonideal Crystals. Berlin: Springer-Verlag.]). Huang scattering is the DS produced by long-range elastic fields created by point defects in a crystal. For example, Huang scattering has been recently reported in the DS from single crystals of PbZr1−xTixO3 (Burkovsky et al., 2012[Burkovsky, R. G., Bronwald, Y. A., Filimonov, A. V., Rudskoy, A. I., Chernyshov, D., Bosak, A., Hlinka, J., Long, X., Ye, Z.-G. & Vakhrushev, S. B. (2012). Phys. Rev. Lett. 109, 097603.]). The presence of the low-intensity plane suggests that the observed DS from NBT might occur as a result of a similar type of long-range elastic strain field. We should note, however, that there is an important difference between the observed DS and Huang scattering: Huang scattering is symmetrically distributed around a Bragg node, whereas the observed DS in NBT is not.

3.2. Temperature dependence of the scattering intensity

The observed intensity distributions are temperature dependent. Fig. 4[link] displays the RSMs [the same section as in Fig. 3[link](a)] at three temperatures upon heating: 100 K [below the [R3c \mid Cc]P4bm phase transition; Fig. 4[link](a)], 545 K [on approach to the phase transition; Fig. 4[link](b)] and 606 K [above the phase transition; Fig. 4[link](c)]. An animation of the temperature dependence of the RSVs (on both heating and cooling) is available in the supporting information. It shows that all of the scattering described above becomes weaker at higher temperature and below the phase transition. The RSV collected above the phase transition consists of a single Bragg reflection decorated by some very weak DS streaks that extend towards the lower scattering angles; this Bragg peak appears extremely sharp, with a full width at half-maximum of only 0.003 r.l.u. In order to describe quantitatively the thermal evolution of the scattering we will discuss now in turn the behaviours of the Bragg and diffuse scattering features.

[Figure 4]
Figure 4
The temperature dependence of the RSMs around the [032 ]* reciprocal lattice point, as seen on the 0kl plane in Fig. 3[link](a). The first two temperatures, (a) 100 K and (b) 545 K, correspond to the lower-temperature [R3c \mid Cc] phase; (c) 606 K corresponds to the tetragonal P4bm phase. The white and red dashed lines show the crystallographic [032]* and [{ [{02\bar 3} ]^*}] directions, respectively [as in Fig. 3[link](a)]. An animated version of this figure is available in the supporting information.
3.2.1. Temperature dependence of the Bragg scattering: the evidence for low-temperature phase segregation

Fig. 5[link] summarizes the temperature dependence of the radial intensity profile, reconstructed along the [032 ]* reciprocal lattice direction and passing through the overall intensity maximum. For each temperature the one-dimensional radial intensity, R(lr ), is reconstructed from the three-dimensional data as [R({l}_{\rm r}) = \textstyle\int\!\int I(h,{Y}_{\rm r}, {l}_{\rm r})\,{\rm d}h\, {\rm d}{Y}_{\rm r}], where Yr represents the coordinate parallel to the [{ [{02\bar 3} ]^*}] reciprocal lattice direction. The integration was carried out over a 0.02 × 0.02 r.l.u. square. The radial direction lr is shown by the arrow in Fig. 5[link](a), the borders of the integration are shown by the dashed lines, and the resultant radial profile for the 300 K data is shown in Fig. 5[link](b). The thermal evolution of this profile describes the radial splitting of the Bragg reflection as a function of temperature (Fig. 5[link]c).

[Figure 5]
Figure 5
The temperature dependence of the radial scattering intensity profile along the [032 ]* direction. (a) The h0lr reciprocal space map, showing the radial direction along which the profile is taken (arrow) and the corresponding integration box (dashed lines); (b) the resulting intensity profile for the 300 K data; (c) a false-colour map showing the temperature dependence of the radial profile, the extracted peak positions being highlighted by the solid and dashed lines; (d) the extracted peak intensities. The nominal temperature of the phase transition is shown by the vertical dashed line at 585 K; the average temperature of thermal depoling (known from previous work) is shown by the vertical dashed line at 455 K. The intensity of the matrix peak can only be followed until 570 K.

Fig. 5[link](c) shows that far from the phase transition both island and matrix Bragg peaks move to larger d spacing (lower lr values) upon heating, which is consistent with thermal expansion. However, at ∼455 K (i.e. ∼120 K below the phase transition), some peculiarities appear: firstly, the position of the island peak reaches a point of inflection and begins to behave as though the corresponding sample volumes had negative thermal expansion. This movement allows the island and matrix Bragg peaks to approach each other, yet as they do so the matrix peak disappears. The island peak continues into the high-temperature phase and becomes the very sharp single Bragg reflection associated with the tetragonal structure. Fig. 5[link](d) shows the details of the temperature dependence of the matrix and island intensities (IM and II), reconstructed along the dashed lines in Fig. 5[link](c). It shows that the matrix peak decays linearly with the temperature, becoming immeasurably small a few kelvin before the nominal phase transition temperature. At the same time the island peak reduces by just 50% until it flows into the single sharp Bragg peak observed in the tetragonal phase.

Although the temperature dependence of the matrix and island peak positions looks similar to the behaviour expected for a ferroelastic phase transition, the temperature dependence of their intensities and the presence of diffuse scattering indicate a more complex picture. The continuation of the high-temperature Bragg peak into the island Bragg peak at lower temperatures and the absence of the matrix peak a few kelvin before the phase transition suggest that the island peak is a persistence of the tetragonal phase below the transition. We must assume some phase segregation, so that matrix peaks are diffracted by the dominating volumes of monoclinic/rhombohedral phase, whereas island peaks are diffracted from the tetragonal inclusions, remnants of the high-temperature tetragonal phase. Considering the lattice mismatch between higher- and lower-temperature phases we must also assume that such phase separation creates long-range deformation fields and produces the characteristic diffuse scattering pattern.

Note that similar phase segregation/local microstructure models in NBT appear in the literature. For example, it resembles the model of tetragonal inclusions in a rhombohedral matrix suggested as a result of transmission electron microscopy imaging of NBT (Beanland & Thomas, 2011[Beanland, R. & Thomas, P. A. (2011). Scr. Mater. 65, 440-443.]; Yao et al., 2012[Yao, J., Monsegue, N., Murayama, M., Leng, W., Reynolds, W. T., Zhang, Q., Luo, H., Li, J., Ge, W. & Viehland, D. (2012). Appl. Phys. Lett. 100, 012901.]). It agrees with the observation of Rao, Datta et al. (2013[Rao, B. N., Datta, R., Chandrashekaran, S., Mishra, D. K., Sathe, V., Senyshyn, A. & Ranjan, R. (2013). Phys. Rev. B, 88, 224103.]) and Liu et al. (2012[Liu, Y., Withers, R. L., Wang, J., Norén, L., Studer, A. J. & Li, Y. (2012). J. Adv. Dielect. 02, 1230012.]), who reported the appearance of in-phase octahedral tilt regions ( a0a0c+ octahedral tilt systems), consistent with tetragonal P4bm symmetry, in the [R3c \mid Cc] phase. Similar formation of a0a0c+ planar defects was reported in 0.96NBT–0.04BT single crystals (Daniels et al., 2011[Daniels, J. E., Jo, W., Rödel, J., Rytz, D. & Donner, W. (2011). Appl. Phys. Lett. 98, 252904.], 2012[Daniels, J. E., Jo, W. & Donner, W. (2012). JOM, 64, 174-180.]), where [ {\langle100\rangle ^*}] diffuse scattering rods were observed around half-integer reflections. Such planar defects were described as `stacking faults', separating two rhombohedral a- a- a- domains. The tetragonal symmetry in such `stacking faults' was also demonstrated by Beanland (2011[Beanland, R. (2011). Acta Cryst. A67, 191-199.]). Alternatively, the segregations in the lower-temperature phase of NBT have been also discussed by Gröting et al. (2011[Gröting, M., Hayn, S. & Albe, K. (2011). J. Solid State Chem. 184, 2041-2046.]), who performed first-principle calculations to test the possible chemical ordering on the A site and suggested that such short-range ordering (with alternating layers of Bi and Na along 〈100〉) is possible below ∼570 K and could provide nucleation sites for larger regions.

3.2.2. Thermal expansion coefficients of the matrix and island phases

This assumption of phase segregation below the phase transition is further supported by some simple macroscopic strain analysis. The relative separation between the island and matrix Bragg peaks at 300 K (Fig. 5[link]b) is [{{\Delta {l}_{\rm r}}/{{l}_{\rm r}}} = 0.59] (4)%. It matches the separation between the lattice parameters of the room-temperature phase and the lattice parameters of the high-temperature tetragonal phase reported by Jones & Thomas (2002[Jones, G. O. & Thomas, P. A. (2002). Acta Cryst. B58, 168-178.]): (cT673K-aR273K)/aR273K = 0.52 (1)% [here cT673K = 3.9073 (2) Å is the tetragonal c lattice parameter at 673 K and aR273K = 3.8869 (2) Å is the pseudocubic a lattice parameter at room temperature]. We elaborated on this phase segregation idea by analysing the linear thermal expansion corresponding to each of the above phases. This thermal expansion was calculated according to [\alpha =] - (1 /Lr) dLr/ dT [Lr denotes the positions of the maxima of the peak(s)] and is shown in Fig. 6[link]. The individual thermal behaviours of the phases differ. The position of the island peak appears almost temperature independent; it exhibits little overall thermal expansion between 40 and 573 K, reaching the maximum of 0.45 × 10−5 K−1 at around 320 K. The position of the matrix peak adopts a more typical thermal expansion over this temperature range; it is comparable to the thermal expansion previously reported for NBT single crystals (1.50–1.75×10-5 K−1) according to Park et al. (1996[Park, S. E., Chung, S. J. & Kim, I. T. (1996). J. Am. Ceram. Soc. 79, 1290-1296.]). This behavioural difference diverges further as the phase transition is approached, as the matrix peak enters a region of negative thermal expansion as previously mentioned. The systematically lower thermal expansion of the tetragonal island phase suggests that the regions of this symmetry might be trapped by the monoclinic/rhombohedral structure that develops.

[Figure 6]
Figure 6
The linear thermal expansion coefficient (TEC), calculated using the positions of the matrix and island peaks. The range of TEC coefficients reported by Park et al. (1996[Park, S. E., Chung, S. J. & Kim, I. T. (1996). J. Am. Ceram. Soc. 79, 1290-1296.]) is marked by the grey rectangle.
3.2.3. Temperature dependence of the diffuse streaks

Fig. 7[link] (organized in a similar way to Fig. 5[link]) shows the temperature dependence of the diffuse scattering. The intensity profile in Fig. 7[link](b) is reconstructed from the three-dimensional data as [D(h) = \textstyle\int\!\int I(h,{Y}_{\rm r}, {l}_{\rm r})\, {\rm d}{Y}_{\rm r}\,{\rm d}{l}_{\rm r}], where the integration was carried out within a 0.015 × 0.015 r.l.u. box. Fig. 7[link](a) indicates the h direction and the corresponding integration box with an arrow and dashed lines, respectively. Fig. 7[link](b) shows the as-defined profile for the 300 K data. The temperature dependence of this profile is then displayed in Fig. 7[link](c). Fig. 7[link](d) follows the intensity of the diffuse streaks, Id(T), reconstructed along their maxima [shown by the dashed lines in Fig. 7[link](c)]. The intensity of the DS streaks decreases as the phase transition is approached, in a fashion very reminiscent of the matrix Bragg peak.

[Figure 7]
Figure 7
The temperature dependence of the diffuse scattering intensity profile, D(h), along the [100]* direction. (a) The h0lr reciprocal space map, showing the direction along which the D(h ) profile is taken (arrow) and the corresponding integration box (dashed lines); (b) the resulting intensity profile for the 300 K data; (c) false-colour map showing the temperature dependence of the intensity profile, the extracted peak positions of the DS streaks being highlighted by the dashed lines; (d) the extracted peak intensities (averaged over both streaks). The vertical dashed lines in both (c) and (d) mark the same temperatures as in Fig. 5[link].
3.2.4. Relationship between Bragg and diffuse scattering

As a last step we investigated the relationship between the temperature dependences of the island and matrix Bragg peaks and the DS. We plot all these dependencies in the temperature range below 570 K, where the intensity of both peaks is measurable. Fig. 8[link] shows that the functional dependence of the DS intensity on the matrix Bragg peak intensity can be described by two linear regression intervals: below ∼425 K and above ∼495 K. The change of the linear regression coefficient between these temperatures points to a possible `virtual' phase transition, which describes the change of the balance between long-range-ordered structure (responsible for the Bragg peak) and structural disorder (responsible for the DS).

[Figure 8]
Figure 8
Relationships between the intensities of the matrix Bragg peak, diffuse streaks (diamonds) and island (circles) Bragg peaks. The dashed red lines display the results of the linear regression in the two different temperature ranges: below 425 K and above 495 K. The change of the linear regression coefficient connecting the intensity of the diffuse scattering as a function of the matrix peak intensity points to the `virtual' transition, involving the modification of the fine disorder parameter at these temperatures.

4. Conclusion

In conclusion, we have reconstructed the fine details of single-crystal DS from NBT with a resolution of ∼10−3 r.l.u. Then we have carefully inspected the topology and temperature dependence of the scattering and followed their evolution on the approach to and through the [R3c \mid Cc] to P4bm structural phase transition. Our data show that such a phase transition must generate the complex bulk microstructure of the [R3c \mid Cc] phase and a correspondingly characteristic X-ray scattering pattern: the Bragg peak in the [R3c \mid Cc] phase separates into two components, the weaker of which (`island' peak) behaves as a representative of the persistence of the tetragonal P4bm phase, while another, stronger peak (`matrix' peak) emerges just below the phase transition temperature. Both peaks are decorated by L-shaped DS streaks: the stronger streaks flow out of the island Bragg peak and extend towards lower scattering angles/higher d spacing; the weaker streaks flow out of the matrix Bragg peak, extending towards higher scattering angles/lower d spacing. The two Bragg peaks, together with their associated DS, are separated by a plane of low intensity which is reminiscent of that observed because of Huang scattering. We have also found that the relative separation between the matrix and island Bragg peaks matches the relative separation between the lattice parameters of the previously reported high-temperature (P4bm) and low-temperature [(R3c \mid Cc)] phases (Jones & Thomas, 2002[Jones, G. O. & Thomas, P. A. (2002). Acta Cryst. B58, 168-178.]).

The geometry and the temperature dependence of the scattering patterns suggest that the low-temperature phase may be a phase coexistence in which volumes of higher-temperature P4bm phase persist below the phase transition into the low-temperature [R3c \mid Cc] phase. Such microstructure must create a pattern of the long-range strain fields of monoclinic (m) point symmetry in both [R3c \mid Cc] matrix and P4bm island phase components. This model may account for the multiple controversies about the structure and symmetry of the low-temperature [R3c \mid Cc] phase: ranging from purely rhombohedral R3c in the defect-free areas (Beanland & Thomas, 2014[Beanland, R. & Thomas, P. A. (2014). Phys. Rev. B, 89, 174102.]) to long-range monoclinic Cc (Gorfman & Thomas, 2010[Gorfman, S. & Thomas, P. A. (2010). J. Appl. Cryst. 43, 1409-1414.]; Aksel, Forrester, Jones et al., 2011[Aksel, E., Forrester, J. S., Jones, J. L., Thomas, P. A., Page, K. & Suchomel, M. R. (2011). Appl. Phys. Lett. 98, 152901.]; Ma et al., 2013[Ma, C., Guo, H. & Tan, X. (2013). Adv. Funct. Mater. 23, 5261-5266.]) and the combination of both (Rao, Datta et al., 2013[Rao, B. N., Datta, R., Chandrashekaran, S., Mishra, D. K., Sathe, V., Senyshyn, A. & Ranjan, R. (2013). Phys. Rev. B, 88, 224103.]). Considering this model of phase coexistence, it becomes possible to explain why the apparent symmetry depends on the length scale of the probe, the type of sample, doping and even the preparation history, in which case the local concentration of tetragonal inclusions may differ from sample to sample.

We must emphasize that more specific details of the structural disorder responsible for the asymmetric L-shaped diffuse scattering remain unknown. The topological similarity of the observed DS to Huang scattering suggests that the underlying structural disorder may originate from the long-range elastic deformation field, extending both inwards and outwards from the segregated tetragonal P4bm phase discussed above. However, Huang scattering does not account for the observed asymmetry of the DS streaks. Therefore, some essential modifications of the corresponding model of the structural disorder must be considered. For example, it is known that NBT may show significant positional disorder (e.g. Keeble et al., 2013[Keeble, D. S., Barney, E. R., Keen, D. A., Tucker, M. G., Kreisel, J. & Thomas, P. A. (2013). Adv. Funct. Mater. 23, 185-190.]) of the Bi atoms. We may assume that any long-range deformation field may trigger local atomic displacements, thus modifying the structural disorder. Such possible involvement of Bi displacements can be also supported by the fact that the reported X-ray diffuse scattering, which is highly dominated by Bi positions, strongly differs from neutron diffuse scattering (Ge et al., 2013[Ge, W., Devreugd, C. P., Phelan, D., Zhang, Q., Ahart, M., Li, J., Luo, H., Boatner, L. A., Viehland, D. & Gehring, P. M. (2013). Phys. Rev. B, 88, 174115.]).

Despite remaining uncertainties, our studies evidence a `virtual' phase transition that marks a change between two different temperature dependencies of the scattering intensities. The apparent match of the `virtual' phase transition temperature in NBT with the temperature of thermal depoling is an interesting coincidence that merits further investigation.

Supporting information


Acknowledgements

We acknowledge Dr Dmitry Chernyshov (Swiss–Norwegian Beamlines at the ESRF, Grenoble, France) and Dr Alexei Bosak (ESRF, Grenoble, France) for stimulating discussions and Dr Steven Collins (Diamond Light Source, Didcot, UK) for experimental support.

References

First citationAksel, E., Forrester, J. S., Jones, J. L., Thomas, P. A., Page, K. & Suchomel, M. R. (2011). Appl. Phys. Lett. 98, 152901.  Web of Science CrossRef Google Scholar
First citationAksel, E., Forrester, J. S., Kowalski, B., Deluca, M., Damjanovic, D. & Jones, J. L. (2012). Phys. Rev. B, 85, 024121.  Web of Science CrossRef Google Scholar
First citationAksel, E., Forrester, J. S., Kowalski, B., Jones, J. L. & Thomas, P. A. (2011). Appl. Phys. Lett. 99, 222901.  Web of Science CrossRef Google Scholar
First citationAksel, E., Forrester, J. S., Nino, J. C., Page, K., Shoemaker, D. P. & Jones, J. L. (2013). Phys. Rev. B, 87, 104113.  CrossRef Google Scholar
First citationBalagurov, A. M., Koroleva, E. Y., Naberezhnov, A. A., Sakhnenko, V. P., Savenko, B. N., Ter-Oganessian, N. V. & Vakhrushev, S. B. (2006). Phase Transitions, 79, 163–173.  CrossRef CAS Google Scholar
First citationBeanland, R. (2011). Acta Cryst. A67, 191–199.  CrossRef IUCr Journals Google Scholar
First citationBeanland, R. & Thomas, P. A. (2011). Scr. Mater. 65, 440–443.  CrossRef CAS Google Scholar
First citationBeanland, R. & Thomas, P. A. (2014). Phys. Rev. B, 89, 174102.  CrossRef Google Scholar
First citationBosak, A., Chernyshov, D., Vakhrushev, S. & Krisch, M. (2012). Acta Cryst. A68, 117–123.  Web of Science CrossRef CAS IUCr Journals Google Scholar
First citationBurkovsky, R. G., Bronwald, Y. A., Filimonov, A. V., Rudskoy, A. I., Chernyshov, D., Bosak, A., Hlinka, J., Long, X., Ye, Z.-G. & Vakhrushev, S. B. (2012). Phys. Rev. Lett. 109, 097603.  Web of Science CrossRef PubMed Google Scholar
First citationCarter, J., Aksel, E., Iamsasri, T., Forrester, J. S., Chen, J. & Jones, J. L. (2014). Appl. Phys. Lett. 104, 112904.  CrossRef Google Scholar
First citationDaniels, J. E., Jo, W. & Donner, W. (2012). JOM, 64, 174–180.  Web of Science CrossRef CAS Google Scholar
First citationDaniels, J. E., Jo, W., Rödel, J., Rytz, D. & Donner, W. (2011). Appl. Phys. Lett. 98, 252904.  Web of Science CrossRef Google Scholar
First citationDorcet, V. & Trolliard, G. (2008). Acta Mater. 56, 1753–1761.  Web of Science CrossRef CAS Google Scholar
First citationDorcet, V., Trolliard, G. & Boullay, P. (2008). Chem. Mater. 20, 5061–5073.  Web of Science CrossRef CAS Google Scholar
First citationEkstein, H. (1945). Phys. Rev. 68, 120–124.  CrossRef CAS Google Scholar
First citationForonda, H., Deluca, M., Aksel, E., Forrester, J. S. & Jones, J. L. (2014). Mater. Lett. 115, 132–135.  CrossRef CAS Google Scholar
First citationGe, W., Devreugd, C. P., Phelan, D., Zhang, Q., Ahart, M., Li, J., Luo, H., Boatner, L. A., Viehland, D. & Gehring, P. M. (2013). Phys. Rev. B, 88, 174115.  CrossRef Google Scholar
First citationGlazer, A. M. (1972). Acta Cryst. B28, 3384–3392.  CrossRef CAS IUCr Journals Web of Science Google Scholar
First citationGorfman, S., Glazer, A. M., Noguchi, Y., Miyayama, M., Luo, H. & Thomas, P. A. (2012). J. Appl. Cryst. 45, 444–452.  Web of Science CrossRef CAS IUCr Journals Google Scholar
First citationGorfman, S. & Thomas, P. A. (2010). J. Appl. Cryst. 43, 1409–1414.  Web of Science CrossRef CAS IUCr Journals Google Scholar
First citationGröting, M., Hayn, S. & Albe, K. (2011). J. Solid State Chem. 184, 2041–2046.  Google Scholar
First citationGröting, M., Kornev, I., Dkhil, B. & Albe, K. (2012). Phys. Rev. B, 86, 134118.  Google Scholar
First citationHiruma, Y., Nagata, H. & Takenaka, T. (2009). J. Appl. Phys. 105, 084112.  Web of Science CrossRef Google Scholar
First citationJones, G. O. & Thomas, P. A. (2000). Acta Cryst. B56, 426–430.  Web of Science CrossRef CAS IUCr Journals Google Scholar
First citationJones, G. O. & Thomas, P. A. (2002). Acta Cryst. B58, 168–178.  Web of Science CrossRef CAS IUCr Journals Google Scholar
First citationKeeble, D. S., Barney, E. R., Keen, D. A., Tucker, M. G., Kreisel, J. & Thomas, P. A. (2013). Adv. Funct. Mater. 23, 185–190.  Web of Science CrossRef CAS Google Scholar
First citationKraft, P., Bergamaschi, A., Broennimann, Ch., Dinapoli, R., Eikenberry, E. F., Henrich, B., Johnson, I., Mozzanica, A., Schlepütz, C. M., Willmott, P. R. & Schmitt, B. (2009). J. Synchrotron Rad. 16, 368–375.  Web of Science CrossRef CAS IUCr Journals Google Scholar
First citationKreisel, J., Bouvier, P., Dkhil, B., Thomas, P. A., Glazer, A. M., Welberry, T., Chaabane, B. & Mezouar, M. (2003). Phys. Rev. B, 68, 014113.  CrossRef Google Scholar
First citationKrivoglaz, M. A. (1996). X-ray and Neutron Diffraction in Nonideal Crystals. Berlin: Springer-Verlag.  Google Scholar
First citationLevin, I. & Reaney, I. M. (2012). Adv. Funct. Mater. 22, 3445–3452.  Web of Science CrossRef CAS Google Scholar
First citationLiu, Y., Withers, R. L., Wang, J., Norén, L., Studer, A. J. & Li, Y. (2012). J. Adv. Dielect. 02, 1230012.  CrossRef Google Scholar
First citationMa, C., Guo, H. & Tan, X. (2013). Adv. Funct. Mater. 23, 5261–5266.  Web of Science CrossRef CAS Google Scholar
First citationMeyer, K.-C., Gröting, M. & Albe, K. (2015). J. Solid State Chem. 227, 117–122.  CrossRef CAS Google Scholar
First citationMitchell, R. H. (2003). Perovskites: Modern and Ancient. Thunder Bay: Almaz-Press.  Google Scholar
First citationPark, S. E., Chung, S. J. & Kim, I. T. (1996). J. Am. Ceram. Soc. 79, 1290–1296.  CrossRef CAS Google Scholar
First citationPaściak, M., Heerdegen, A., Goossens, D. J., Whitfield, R. E., Pietraszko, A. & Welberry, T. R. (2012). Met. Mater. Trans. A, 44, 87–93.  Google Scholar
First citationRao, B. N., Datta, R., Chandrashekaran, S., Mishra, D. K., Sathe, V., Senyshyn, A. & Ranjan, R. (2013). Phys. Rev. B, 88, 224103.  Web of Science CrossRef Google Scholar
First citationRao, B. N., Fitch, A. & Ranjan, R. (2013). Phys. Rev. B, 87, 060102.  CrossRef Google Scholar
First citationRao, B. N. & Ranjan, R. (2012). Phys. Rev. B, 86, 134103.  CrossRef Google Scholar
First citationShuvaeva, V. A., Zekria, D., Glazer, A. M., Jiang, Q., Weber, S. M., Bhattacharya, P. & Thomas, P. A. (2005). Phys. Rev. B, 71, 174114.  Web of Science CrossRef Google Scholar
First citationStock, C., Xu, G., Gehring, P. M., Luo, H., Zhao, X., Cao, H., Li, J. F., Viehland, D. & Shirane, G. (2007). Phys. Rev. B, 76, 064122.  CrossRef Google Scholar
First citationTakenaka, T., Nagata, H. & Hiruma, Y. (2008). Jpn. J. Appl. Phys. 47, 3787–3801.  Web of Science CrossRef CAS Google Scholar
First citationThomas, P. A., Trujillo, S., Boudard, M., Gorfman, S. & Kreisel, J. (2010). Solid State Sci. 12, 311–317.  Web of Science CrossRef CAS Google Scholar
First citationVakhrushev, S. B., Isupov, V., Kvyatkovsky, B. E., Okuneva, N. M., Pronin, I. P., Smolensky, G. A. & Syrnikov, P. P. (1985). Ferroelectrics, 63, 153–160.  CrossRef CAS Google Scholar
First citationXu, G., Zhong, Z., Bing, Y., Ye, Z.-G. & Shirane, G. (2006). Nat. Mater. 5, 134–140.  Web of Science CrossRef PubMed CAS Google Scholar
First citationYao, J., Ge, W., Luo, L., Li, J., Viehland, D. & Luo, H. (2010). Appl. Phys. Lett. 96, 222905.  CrossRef Google Scholar
First citationYao, J., Monsegue, N., Murayama, M., Leng, W., Reynolds, W. T., Zhang, Q., Luo, H., Li, J., Ge, W. & Viehland, D. (2012). Appl. Phys. Lett. 100, 012901.  CrossRef Google Scholar

This is an open-access article distributed under the terms of the Creative Commons Attribution (CC-BY) Licence, which permits unrestricted use, distribution, and reproduction in any medium, provided the original authors and source are cited.

Journal logoJOURNAL OF
APPLIED
CRYSTALLOGRAPHY
ISSN: 1600-5767
Follow J. Appl. Cryst.
Sign up for e-alerts
Follow J. Appl. Cryst. on Twitter
Follow us on facebook
Sign up for RSS feeds