X-ray diffractometry for the structure determination of a submicrometre single powder grain

CROSSMARK_Color_square_no_text.svg

aJASRI/SPring-8, 1-1-1 Kouto, Sayo-cho, Sayo-gun, Hyogo 679-5198, Japan, bJapan Science and Technology Agency, CREST, 5 Sanbancho, Chiyoda-ku, Tokyo 102-0075, Japan, cDepartment of Applied Chemistry, Faculty of Science and Engineering, Chuo University, 1-13-27 Kasuga, Bunkyo-ku, Tokyo 112-8551, Japan, dGraduate School of Material Science, University of Hyogo, 3-2-1 Kouto, Kamigori-cho, Ako-gun, Hyogo 678-1297, Japan, eRIKEN SPring-8 Center, Harima Institute, 1-1-1 Kouto, Sayo-cho, Sayo-gun, Hyogo 679-5148, Japan, fThe Graduate School of Pure and Applied Sciences, University of Tsukuba, Tenodai, Tsukuba, Ibaraki 305-8571, Japan, gDepartment of Physical Science, Graduate School of Science, Hiroshima University, 1-3-1 Kagamiyama, Higashi-Hiroshima, Hiroshima 739-8526, Japan, and hDepartment of Advanced Materials Science, School of Frontier Sciences, The University of Tokyo, 5-1-5 Kashiwanoha, Kashiwa-shi, Chiba 277-8561, Japan
*Correspondence e-mail: kimuras@spring8.or.jp

(Received 24 December 2008; accepted 24 February 2009; online 1 April 2009)

A high-precision diffractometer has been developed for the structure analysis of a submicrometre-scale single grain of a powder sample at the SPring-8 BL40XU undulator beamline. The key design concept is the combination of a stable focused synchrotron radiation beam and the precise axis control of the diffractometer, which allows accurate diffraction intensity data of a submicrometre-scale single powder grain to be measured. The phase zone plate was designed to create a high-flux focused synchrotron radiation beam. A low-eccentric goniometer and high-precision sample positioning stages were adopted to ensure the alignment of a micrometre-scale focused synchrotron radiation beam onto the submicrometre-scale single powder grain. In order to verify the diffractometer performance, the diffraction pattern data of several powder grains of BaTiO3, of dimensions ∼600 × 600 × 300 nm, were measured. By identifying the diffraction data set of one single powder grain, the crystal structure was successfully determined with a reliable factor of 5.24%.

1. Introduction

Up to now, the structure identification and characterization of various new materials have been carried out by powder diffraction experiments as newly synthesized materials are, in most cases, obtained in powder and/or in polycrystalline forms. This research technical trend has been accelerated by the high-photon-flux monochromatic X-rays of synchrotron radiation in addition to the progress of computers and software for structure determination. Consequently, the development of an ab initio structure analysis technique, which denotes unknown structure determination, is now one of the most topical research subjects in powder crystallography (David et al., 2002[David, W. I. F., Shankland, K., McCusker, L. B. & Baerlocher, Ch. (2002). Editors. Structure Determination from Powder Diffraction Data, pp. 1-11. Oxford University Press.]; David & Shankland, 2008[David, W. I. F. & Shankland, K. (2008). Acta Cryst. A64, 52-64.]). On the other hand, an X-ray synchrotron radiation beam with high brilliance and small divergence allows an alternative method to be suggested, which can determine the crystal structure of a micrometre- or submicrometre-scale single crystal corresponding to a single grain of a powder sample. In fact, some structure determinations of a few micrometre-sized single crystals were recently reported using a synchrotron radiation focusing technique (Riekel et al., 2005[Riekel, C., Burghammer, M. & Schertler, G. (2005). Curr. Opin. Struct. Biol. 15, 556-562.]; Volkringer et al., 2007[Volkringer, C., Popov, D., Loiseau, T., Guillou, N., Ferey, G., Haouas, M., Taulelle, F., Mellot-Draznieks, C., Burghammer, M. & Riekel, C. (2007). Nat. Mater. 6, 760-764.]). Before those works, the Laue method, which uses an intense white synchrotron radiation beam instead of a focused monochromatic beam, was also performed on a submicrometre crystal to measure the intensity data efficiently (Ohsumi et al., 1991[Ohsumi, K., Hagiya, K. & Ohmasa, M. (1991). J. Appl. Cryst. 24, 340-348.]). However, the conventional structure determination of a submicrometre-scale single crystal has not yet been reported. This is mainly due to three technical difficulties which must be overcome: the accurate intensity data collection of very weak diffraction spots, the precise centring of the invisible sample, and the infallible manipulation of a submicrometre-scale single crystal. The combination of the synchrotron radiation focusing technique and the precise axis control of the diffractometer is a solution for the first and second difficulties. The latest focusing technique for a synchrotron radiation diffraction experiment can firmly produce a micrometre-scale high-flux synchrotron radiation beam. The precise axis control enables the submicrometre-scale sample to be moved and kept within the micrometre-scale focused synchrotron radiation beam. We have therefore developed and optimized a high-precision diffractometer which combines a synchrotron radiation focusing technique and low eccentric sample rotation at the SPring-8 BL40XU undulator beamline, to enable the structure analysis of a submicrometre-scale single powder grain. As for the third difficulty, since the development of the systematic manipulation techniques to select and capture one single grain of powder sample is still in progress, several submicrometre-scale single powder grains have been attached to a fine glass fibre by means of the conventional sample manipulation technique.

From a technical viewpoint, the structure analysis of a submicrometre-scale single powder grain has great advantages for applications to structural materials science research. Firstly, we can remove the intrinsic problem in the powder diffraction method, peak overlapping, which causes ambiguities in the determined structure in most cases, since a single powder grain can be mostly treated as a single crystal. Secondly, submicrometre-scale samples enable us to measure data free from extinction and/or absorption correction.

Another advantage arises in the case of observations of photo-induced phase transition (PIPT). For laser-pump and synchrotron-radiation-probe experiments, we can avoid the mismatch between the penetration depths of laser and X-rays since a typical penetration depth of laser light is of the order of 1 µm. This indicates near 100% yield of PIPT, which greatly improves the accuracy of the structure analysis of PIPT, is achievable with a submicrometre-scale single powder grain.

Practically, the structure analysis of a submicrometre-scale single powder grain can be directly applied to the research of the grain-size-dependent structure–property relationship. One of the most attractive examples is a barium titanate (BaTiO3) fine particle, which shows a phase transition from tetragonal to cubic as the particle size decreases. Some diffraction studies of the size effect of BaTiO3 were carried out using the powder diffraction method (Aoyagi et al., 2002[Aoyagi, S., Kuroiwa, Y., Sawada, A., Yamashita, I. & Atake, T. (2002). J. Phys. Soc. Jpn, 71, 1218-1221.]). However, the powder diffraction method had the following disadvantages: the obtained structural parameters are the averaged information from various size particles in the powder sample; in addition, the peak overlapping becomes more serious owing to the peak profile broadening caused by the small particle size. The structure analysis of a single powder grain could overcome these difficulties because the diffraction peaks are isolated geometrically.

In this article we illustrate the concepts and features of the high-precision diffractometer for the structure analysis of a single powder grain, with an example of the structure analysis of a BaTiO3 fine particle of dimensions ∼600 × 600 × 300 nm.

2. Fundamental design of the high-precision diffractometer

The following qualifications are essential to complete the high-precision diffractometer: (i) high photon flux density of incident synchrotron radiation beam; (ii) low background intensity; (iii) easy alignment and high-performance focusing system; (iv) stable and precise axis rotation of the diffractometer.

Regarding qualifications (i) and (ii), we installed the diffractometer with the synchrotron radiation focusing system at the SPring-8 BL40XU helical undulator beamline (Inoue et al., 2001[Inoue, K., Oka, T., Suzuki, T., Yagi, N., Takeshita, K., Goto, S. & Ishikawa, T. (2001). Nucl. Instrum. Methods Phys. Res. A, 467-468, 674-677.]; Kimura et al., 2007[Kimura, S., Moritomo, Y., Tanaka, Y., Tanaka, H., Toriumi, K., Kato, K., Yasuda, N., Fukuyama, Y., Kim, J. E., Murayama, H. & Takata, M. (2007). AIP Conf. Proc. 879, 1238-1241.]). Fig. 1(a)[link] shows the experimental set-up of the high-precision diffractometer system, and Fig. 1(b)[link] is a photograph of the high-precision diffractometer. Fine focusing of the synchrotron radiation beam enables us to produce the incident synchrotron radiation beam with high photon flux density and small beam size, which improves the signal-to-background ratio because most of the focused synchrotron radiation beam can be incident on the sample.

[Figure 1]
Figure 1
(a) Schematic diagram of the experimental set-up of the high-precision diffractometer system. (b) Photograph of the high-precision diffractometer. The red arrow and yellow box indicate the synchrotron radiation beam and the zone plate focusing optics, respectively.

For qualification (iii), we adopted a phase zone plate to focus the synchrotron radiation beam as on-axis focusing is convenient for diffraction measurements and tuning the focused beam size is easy by adjusting the longitudinal position of the phase zone plate.

Qualification (iv) is key for the structure analysis of a submicrometre-scale single powder grain. The diffraction data are measured in the oscillation mode, which is the same as in single-crystal structure analysis. In order to collect sufficiently accurate diffraction data, the submicrometre-scale single powder grain must be kept within the focused X-ray beam during the measurement. To this end, high-precision ω and 2θ rotation stages were installed in the diffractometer. To avoid eccentric rotation owing to gravitational influences on the rotation axis, vertical ω and 2θ rotation axes were adopted. The vertical rotation axis is not usually used for synchrotron radiation diffraction experiments because of horizontal polarization of the synchrotron radiation beam. However, a helical undulator, which radiates the circularly polarized synchrotron radiation beam, enabled us to use the vertical axis rotation stages.

Another advantage of the helical undulator is that the higher harmonics are emitted towards an off-axial beam direction. By extracting the central part of the radiation, therefore, the high-photon-flux beam (∼1015 photons s−1) with narrow peak-energy width (ΔE/E ≃ 2%) can be used for quasi-monochromatic synchrotron radiation X-rays. The fundamental radiation can be selected from 8 to 17 keV by changing the undulator gap. A further monochromated synchrotron radiation beam (ΔE/E ≃ 0.02%) is made using a Si(111) channel-cut monochromator.

2.1. Zone plate focusing optics

We designed two different phase zone plates (ZP1 and ZP2), fabricated by the NTT-AT Nanofabrication Corporation (Ozawa et al., 1997[Ozawa, A., Tamamura, T., Ishii, T., Yoshihara, H. & Kagoshima, Y. (1997). Microelectron. Eng. 35, 525-529.]). ZP1 is designed for experiments preferring higher photon energy and high photon flux density such as the structure analysis of a submicrometre-scale single powder grain. On the contrary, ZP2 is designed for experiments such as scanning X-ray microscopy requiring high spatial resolution.

ZP1 has a diameter of 100 µm, an innermost zone radius of 5.0 µm, an outermost zone width of 250 nm and a tantalum thickness of 2.5 µm. The thickness was designed to have maximum diffraction efficiency at 15 keV (∼26%). On the other hand, ZP2 has a diameter of 120 µm, an innermost zone radius of 3.0 µm, an outermost zone width of 75 nm and a tantalum thickness of 750 nm. The ideal diffraction efficiency is 12% at 8 keV. The focal lengths of ZP1 and ZP2 are 300 and 50 mm for 15 and 8 keV, respectively.

Fig. 2[link] shows details of the zone plate focusing optics, which has two independent XYZ positioning stages that align the positions of the phase zone plate and the order-sorting aperture (OSA). To align the sample onto the focused synchrotron radiation beam, an optical microscope (KEYENCE VH-Z100) with a CCD video camera can be inserted on the beam axis with a translation stage (stage x) on which the zone plate optics and the optical microscope are mounted in parallel. The optical microscope has a working distance of 25 mm and a magnification range from 100 to 1000, and a few micrometre-sized samples can be observed on a TV monitor. The position stability and reproducibility of the zone plate optics and the optical microscope are monitored by the linear gauge with 100 nm resolution.

[Figure 2]
Figure 2
Schematic diagram of the zone plate focusing optics. The phase zone plate and OSA are aligned by the XYZ positioning stages. These components are mounted on the same translation stage (stage x), which can be moved by 60 mm on the aligned light axis to enable sample centring using the optical microscope. The position repeatability of stage x is monitored by the linear gauge with 100 nm resolution.

2.2. High-precision goniometer

The high-precision goniometer has ω–2θ rotation and XYZ sample positioning stages (Fig. 2[link]). Highly accurate reproducibility of the rotation centre is required for these stages to keep the micrometre-scale focused X-ray beam on the submicrometre-scale single powder grain during a measurement. We therefore adopted a high-precision air-bearing stage (Canon AB-100R) to achieve low eccentric ω-rotation within ±100 nm per 360°. The XYZ sample positioning stages also have 5 nm resolution.

Since the development of the sample manipulation technique of invisible submicrometre-scale powder grains has not yet been completed, several grains are presently attached to the tip of a glass fibre with a diameter of a few micrometres. The centring of the sample can be carried out systematically by using the tip of a glass fibre, not the grains, as a target. Because the diameter of the glass fibre is a few micrometres, the sample alignment can be controlled to less than 1 µm using the large magnification optical microscope inserted on the beam axis.

2.3. X-ray CCD detector

A high-sensitive and low-noise X-ray CCD detector (Rigaku Saturn724), having a 72 × 72 mm image area, and outputting 16-bit 2080 × 2080 pixel two-dimensional data, was used to detect weak diffraction spots of the submicrometre-scale single powder grains. The X-ray CCD is mounted on the arm of the 2θ rotation stage with a translation stage to change the camera distance from 30 to 135 mm. The 2θ resolution can be selected from 0.065° to 0.015° per pixel. The interval of the measurement owing to the dead time of the CCD camera and ω-axis positioning was about 15 s. As a result, the measurement for a data set takes less than 1 h for a micrometre-scale crystal and a few hours for a submicrometre-scale crystal. Rigaku's Rapid Auto System (Rigaku, 1998[Rigaku Corporation (1998). RAPID-AUTO. Rigaku Corporation, Tokyo, Japan.]) is available for processing the measured diffraction data.

3. Beam size and photon flux on the sample position

The synchrotron radiation beam is pre-focused by two mirrors that are installed in the optics hutch. The focal point of the mirrors is located as the virtual source at 8900 mm upstream of the phase zone plate (Fig. 1a[link]). The size of the virtual source can be tuned to 5 × 5 µm by the mechanical slit.

Without the mechanical slit shaping of the virtual source, the photon flux densities of the 15 keV and 8 keV synchrotron radiation beams in front of the phase zone plate position were 7.9 × 106 and 4.3 × 105 photons s−1 µm−2, respectively. The synchrotron radiation beam is focused by the phase zone plate, and the first-order focused synchrotron radiation beam is only selected with the OSA placed before the sample position. The horizontal and vertical beam sizes at the focal position (i.e. the sample position) were evaluated by a knife-edge scan method using Au meshes. The beam profiles in the vertical direction at the focal position are shown in Fig. 3[link]. Achieved performances of ZP1 and ZP2 are listed in Table 1[link]. In the present study we achieved beam sizes of 1.4 (vertical) × 2.9 (horizontal) µm for 15 keV with ZP1 and 330 × 470 nm for 8 keV with ZP2. The photon flux densities increased to 3.1 × 109 and 1.9 × 109 photons s−1 µm−2. The corresponding gain factors are almost 400 and 4400, respectively. The angular divergence of the focused beam was increased to 0.019° for 15 keV with ZP1 and 0.13° for 8 keV with ZP2. Thus, in the case of ZP2, the effect of the data resolution on structure analysis should be taken into account. It should be noted that further focused beam was available by reducing the virtual source size, even though the flux becomes extremely low. The ultimate beam size of the present system was 79 × 87 nm at 8 keV with a 10 × 10 µm virtual source size. The photon flux decreased to 1.51 × 107 photons s−1, while the photon flux density increased to 2.19 × 109 photons s−1 µm−2.

Table 1
Achieved performances of phase zone plates ZP1 and ZP2

  ZP1 ZP2
Photon energy (keV) 15 8
Beam size, vertical × horizontal (µm) 1.4 × 2.9 0.33 × 0.47
Photon flux (photons s−1) 1.25 × 1010 2.92 × 108
Photon flux density (photons s−1 µm−2) 3.1 × 109 1.9 × 109
Gain factor 400 4400
[Figure 3]
Figure 3
Knife-edge scan intensity data of the 15 and 8 keV microfocusing synchrotron radiation beams in the vertical direction at the focal position (solid circles). Solid and broken lines are derivatives of the measured intensity and the Gaussian fitting profiles, respectively.

4. Structure analysis of a submicrometre-scale BaTiO3 single powder grain

Structure analysis was performed for a submicrometre-scale BaTiO3 single powder grain. The grains of BaTiO3 were attached to the tip of a fine glass fibre with epoxy adhesive by means of an optical microscope and a micromanipulator. Figs. 4(a) and 4(b)[link] show the optical microscope and scanning electron microscope (SEM) images of the tip of a fine glass fibre, respectively. Several BaTiO3 grains were attached to the glass fibre. The maximum grain size was about 600 × 600 × 300 nm.

[Figure 4]
Figure 4
Photographs of BaTiO3 powder grains attached to the tip of the fine glass fibre: (a) optical-microscope image. (b) SEM image of the same sample. The size of the large grain is about 600 × 600 × 300 nm. A and B in each figure show the positions of existing BaTiO3 grains. (c) Measured diffraction image of BaTiO3 grains. All measured images are overlapped on one image to see Bragg diffraction spots clearly. The vertical and horizontal 2θ range of the image are ±45° and −30–60°, respectively. The inset is a 50% probability level ORTEP image of the refined BaTiO3 crystal structure.

The diffraction data were collected in the ω-oscillation mode at room temperature. The 15 keV focused synchrotron radiation beam was prepared by ZP1. The calibration of the wavelength was carried out using the powder diffraction pattern of a NIST (National Institute of Standards and Technology) X-ray standard sample, CeO2 (Standard Reference Material 674a). The exposure time and the ω-axis scan step, Δω, were 15 s and 1°, respectively. With this set-up, the 360 diffraction images were collected in 180 min. The overlapped diffraction pattern of the 360 images is shown in Fig. 4(c)[link]. The shape of the diffraction spots does not represent significant deformation caused by the strain of the sample adhered on the glass fibre. The accidentally diffracted spots of the other BaTiO3 grains sometimes interfered in the diffraction pattern during ω-oscillation. These extra spots can be discriminated systematically because the diffraction pattern no longer shows the Debye–Scherrer pattern but the superposition of several single-crystal diffraction patterns. At this moment, however, it is very difficult to directly identify the sample grain corresponding to the diffraction spots among the several sample grains (Fig. 4b[link]).

The crystal structure was solved by direct methods (SHELXS97) and refined by full-matrix least-squares on F2 (SHELXL97) (Sheldrick, 2008[Sheldrick, G. M. (2008). Acta Cryst. A64, 112-122.]). Only the thermal vibration of the Ba atoms was refined anisotropically. The reliability factor of the refinement finally became R1 = 5.24%. The crystal structure and the determined crystallographic parameters are shown in Fig. 4(c)[link] and Table 2[link], respectively.1

Table 2
Crystal data and experimental details for BaTiO3

Formula BaTiO3
Formula weight 233.24
Temperature (K) 300 (2)
Wavelength (Å) 0.83351
Crystal system Tetragonal
Space group P4mm
a (Å) 3.9905 (13)
b (Å) 3.9905 (13)
c (Å) 4.0412 (14)
Volume (Å3) 64.35 (4)
Z 1
Dcalc (Mg m−3) 6.018
Absorption coefficient (mm−1) 18.037
Crystal size (nm) 600 × 600 × 300
θ range (°) 5.92–29.26
Resolution (Å) 4.04–0.85
Reflections collected/unique 468/88
Rint 0.0940
Completeness to θmax 1.00
Data/restraints/parameters 88/0/9
R1 [I > 2σ(I)] 0.0524
Rw [I > 2σ(I)] 0.0994
Goodness of fit 1.168
Number of I > 2σ(I) 85
Largest diffraction peak (e Å−3) 2.079
Largest diffraction hole (e Å−3) −1.980

The crystal system of a 600 × 600 × 300 nm BaTiO3 single powder grain at room temperature was finally determined to be tetragonal. The values of the cell parameters, a = 3.9905 (13) Å and c = 4.0412 (14) Å, correspond to those derived from the powder diffraction studies of a = 3.9950 (1) Å and c = 4.0340 (1) Å for 400 nm-sized particles (Aoyagi et al., 2002[Aoyagi, S., Kuroiwa, Y., Sawada, A., Yamashita, I. & Atake, T. (2002). J. Phys. Soc. Jpn, 71, 1218-1221.]) and 3.99900 (8) Å and 4.03265 (9) Å for 430 nm-sized particles (Yashima et al., 2005[Yashima, M., Hoshina, T., Ishimura, D., Kobayashi, S., Nakamura, W., Tsurumi, T. & Wada, S. (2005). J. Appl. Phys. 98, 014313.]), respectively. This correspondence of the present result with the powder diffraction results proves that the developed diffractometry has great potential for revealing the one-on-one relationship between the crystal size and the crystal structure, if we realise the structure analysis of a single powder grain smaller than 100 nm.

5. Conclusion

The crystal structure of a submicrometre-scale BaTiO3 single powder grain was successfully determined for several single powder grains. This success proves that the diffraction measurement of a single powder grain has a sufficient advantage in the determination of unknown crystal structure for any powder-formed crystalline samples. Thus, the structure analysis of a single powder grain shall become an alternative method of powder diffraction structure analysis.

Note that the present result was obtained from one of the several grains attached on a glass fibre. Thus the manipulation technique to select only one powder grain is the remaining difficulty to be solved.

We have also developed a laser-pump and synchrotron-radiation-probe diffraction technique using the same diffractometer system (Fukuyama et al., 2008a[Fukuyama, Y., Yasuda, N., Kim, J. E., Murayama, H., Ohshima, T., Tanaka, Y., Kimura, S., Kamioka, H., Moritomo, Y., Toriumi, K, Tanaka, H., Kato, K., Ishikawa, T. & Takata, M. (2008a). Rev. Sci. Instrum. 79, 045107.],b[Fukuyama, Y., Yasuda, N., Kim, J. E., Murayama, H., Tanaka, Y., Kimura, S., Kato, K., Kohara, S., Moritomo, Y., Matsunaga, T., Kojima, R., Yamada, N., Tanaka, H., Ohshima, T. & Takata, M. (2008b). Appl. Phys. Express, 1, 045001.]). Now we are ready to apply the structure analysis of a single powder grain for the research of the photo-induced phase transition combined with the pump and probe technique.

Supporting information


Computing details top

Data collection: Rapid Auto(Rigaku); cell refinement: Rapid Auto(Rigaku); data reduction: Rapid Auto(Rigaku); program(s) used to solve structure: SHELXS97 (Sheldrick, 1990); program(s) used to refine structure: SHELXL97 (Sheldrick, 1997).

(I) top
Crystal data top
BaO3TiF(000) = 102
Mr = 233.24Dx = 6.018 Mg m3
Tetragonal, P4mmSynchrotron radiation, λ = 0.83351 Å
a = 3.9905 (13) ŵ = 18.04 mm1
c = 4.0412 (14) ÅT = 300 K
V = 64.35 (4) Å3, white
Z = 10.0006 × 0.0006 × 0.0003 mm
Data collection top
Rigaku Saturn 724
diffractometer
85 reflections with I > 2σ(I)
Radiation source: synchrotron radiation SPring-8 BL40XURint = 0.094
Si(111) Channel Cut monochromatorθmax = 29.3°, θmin = 5.9°
Detector resolution: 29 pixels mm-1h = 24
Oscillation Photograph scansk = 44
468 measured reflectionsl = 44
88 independent reflections
Refinement top
Refinement on F2Primary atom site location: structure-invariant direct methods
Least-squares matrix: fullSecondary atom site location: difference Fourier map
R[F2 > 2σ(F2)] = 0.052 w = 1/[σ2(Fo2) + (0.0473P)2]
where P = (Fo2 + 2Fc2)/3
wR(F2) = 0.102(Δ/σ)max < 0.001
S = 1.17Δρmax = 2.08 e Å3
88 reflectionsΔρmin = 1.98 e Å3
9 parametersAbsolute structure: Flack H D (1983), Acta Cryst. A39, 876-881
0 restraintsAbsolute structure parameter: 0.8 (7)
Crystal data top
BaO3TiZ = 1
Mr = 233.24Synchrotron radiation, λ = 0.83351 Å
Tetragonal, P4mmµ = 18.04 mm1
a = 3.9905 (13) ÅT = 300 K
c = 4.0412 (14) Å0.0006 × 0.0006 × 0.0003 mm
V = 64.35 (4) Å3
Data collection top
Rigaku Saturn 724
diffractometer
85 reflections with I > 2σ(I)
468 measured reflectionsRint = 0.094
88 independent reflections
Refinement top
R[F2 > 2σ(F2)] = 0.0520 restraints
wR(F2) = 0.102Δρmax = 2.08 e Å3
S = 1.17Δρmin = 1.98 e Å3
88 reflectionsAbsolute structure: Flack H D (1983), Acta Cryst. A39, 876-881
9 parametersAbsolute structure parameter: 0.8 (7)
Special details top

Geometry. All e.s.d.'s (except the e.s.d. in the dihedral angle between two l.s. planes) are estimated using the full covariance matrix. The cell e.s.d.'s are taken into account individually in the estimation of e.s.d.'s in distances, angles and torsion angles; correlations between e.s.d.'s in cell parameters are only used when they are defined by crystal symmetry. An approximate (isotropic) treatment of cell e.s.d.'s is used for estimating e.s.d.'s involving l.s. planes.

Refinement. Refinement of F2 against ALL reflections. The weighted R-factor wR and goodness of fit S are based on F2, conventional R-factors R are based on F, with F set to zero for negative F2. The threshold expression of F2 > σ(F2) is used only for calculating R-factors(gt) etc. and is not relevant to the choice of reflections for refinement. R-factors based on F2 are statistically about twice as large as those based on F, and R- factors based on ALL data will be even larger.

Fractional atomic coordinates and isotropic or equivalent isotropic displacement parameters (Å2) top
xyzUiso*/Ueq
Ba10.00000.00000.00000.0073 (10)
Ti10.50000.50000.476 (5)0.005 (2)*
O10.50000.50000.043 (13)0.005 (8)*
O20.00000.50000.533 (13)0.007 (6)*
Atomic displacement parameters (Å2) top
U11U22U33U12U13U23
Ba10.0055 (10)0.0055 (10)0.0108 (16)0.0000.0000.000
Geometric parameters (Å, º) top
Ba1—O2i2.75 (4)Ti1—O22.009 (6)
Ba1—O2ii2.75 (4)Ti1—O1xii2.29 (5)
Ba1—O2iii2.75 (4)Ti1—Ba1xi3.414 (12)
Ba1—O2iv2.75 (4)Ti1—Ba1xiii3.414 (12)
Ba1—O12.827 (3)Ti1—Ba1xiv3.414 (12)
Ba1—O1v2.827 (3)Ti1—Ba1xv3.529 (13)
Ba1—O1vi2.827 (3)Ti1—Ba1xii3.529 (13)
Ba1—O1vii2.827 (3)O1—Ti1iv2.29 (5)
Ba1—O2viii2.94 (4)O1—Ba1xiv2.827 (3)
Ba1—O22.94 (4)O1—Ba1xi2.827 (3)
Ba1—O2ix2.94 (4)O1—Ba1xiii2.827 (3)
Ba1—O2vii2.94 (4)O2—Ti1vi2.009 (6)
Ti1—O11.75 (5)O2—Ba1xvi2.75 (4)
Ti1—O2x2.009 (6)O2—Ba1xii2.75 (4)
Ti1—O2xi2.009 (6)O2—Ba1xiii2.94 (4)
Ti1—O2viii2.009 (6)
O2i—Ba1—O2ii61.8 (9)O1—Ti1—Ba155.7 (3)
O2i—Ba1—O2iii93.2 (16)O2x—Ti1—Ba1130.2 (10)
O2ii—Ba1—O2iii61.8 (9)O2xi—Ti1—Ba1130.2 (10)
O2i—Ba1—O2iv61.8 (9)O2viii—Ti1—Ba159.0 (11)
O2ii—Ba1—O2iv93.2 (16)O2—Ti1—Ba159.0 (11)
O2iii—Ba1—O2iv61.8 (9)O1xii—Ti1—Ba1124.3 (3)
O2i—Ba1—O1123.7 (10)O1—Ti1—Ba1xi55.7 (3)
O2ii—Ba1—O1123.7 (10)O2x—Ti1—Ba1xi130.2 (10)
O2iii—Ba1—O162.0 (9)O2xi—Ti1—Ba1xi59.0 (11)
O2iv—Ba1—O162.0 (9)O2viii—Ti1—Ba1xi59.0 (11)
O2i—Ba1—O1v61.9 (9)O2—Ti1—Ba1xi130.2 (10)
O2ii—Ba1—O1v61.9 (9)O1xii—Ti1—Ba1xi124.3 (3)
O2iii—Ba1—O1v123.7 (10)Ba1—Ti1—Ba1xi71.5 (3)
O2iv—Ba1—O1v123.7 (10)O1—Ti1—Ba1xiii55.7 (3)
O1—Ba1—O1v173 (2)O2x—Ti1—Ba1xiii59.0 (11)
O2i—Ba1—O1vi62.0 (9)O2xi—Ti1—Ba1xiii130.2 (10)
O2ii—Ba1—O1vi123.7 (10)O2viii—Ti1—Ba1xiii130.2 (10)
O2iii—Ba1—O1vi123.7 (10)O2—Ti1—Ba1xiii59.0 (11)
O2iv—Ba1—O1vi62.0 (9)O1xii—Ti1—Ba1xiii124.3 (3)
O1—Ba1—O1vi89.78 (13)Ba1—Ti1—Ba1xiii71.5 (3)
O1v—Ba1—O1vi89.78 (13)Ba1xi—Ti1—Ba1xiii111.5 (6)
O2i—Ba1—O1vii123.7 (10)O1—Ti1—Ba1xiv55.7 (3)
O2ii—Ba1—O1vii62.0 (9)O2x—Ti1—Ba1xiv59.0 (11)
O2iii—Ba1—O1vii62.0 (9)O2xi—Ti1—Ba1xiv59.0 (11)
O2iv—Ba1—O1vii123.7 (10)O2viii—Ti1—Ba1xiv130.2 (10)
O1—Ba1—O1vii89.78 (13)O2—Ti1—Ba1xiv130.2 (10)
O1v—Ba1—O1vii89.78 (13)O1xii—Ti1—Ba1xiv124.3 (3)
O1vi—Ba1—O1vii173 (2)Ba1—Ti1—Ba1xiv111.5 (6)
O2i—Ba1—O2viii176.2 (15)Ba1xi—Ti1—Ba1xiv71.5 (3)
O2ii—Ba1—O2viii120.27 (12)Ba1xiii—Ti1—Ba1xiv71.5 (3)
O2iii—Ba1—O2viii90.60 (11)O1—Ti1—Ba1xv126.9 (3)
O2iv—Ba1—O2viii120.27 (12)O2x—Ti1—Ba1xv50.9 (10)
O1—Ba1—O2viii58.3 (9)O2xi—Ti1—Ba1xv50.9 (10)
O1v—Ba1—O2viii115.7 (10)O2viii—Ti1—Ba1xv119.5 (12)
O1vi—Ba1—O2viii115.7 (10)O2—Ti1—Ba1xv119.5 (12)
O1vii—Ba1—O2viii58.3 (9)O1xii—Ti1—Ba1xv53.1 (3)
O2i—Ba1—O2120.27 (12)Ba1—Ti1—Ba1xv177.4 (6)
O2ii—Ba1—O2176.2 (15)Ba1xi—Ti1—Ba1xv109.76 (3)
O2iii—Ba1—O2120.27 (12)Ba1xiii—Ti1—Ba1xv109.76 (3)
O2iv—Ba1—O290.60 (11)Ba1xiv—Ti1—Ba1xv71.17 (3)
O1—Ba1—O258.3 (9)O1—Ti1—Ba1xii126.9 (3)
O1v—Ba1—O2115.7 (10)O2x—Ti1—Ba1xii119.5 (12)
O1vi—Ba1—O258.3 (9)O2xi—Ti1—Ba1xii119.5 (12)
O1vii—Ba1—O2115.7 (10)O2viii—Ti1—Ba1xii50.9 (10)
O2viii—Ba1—O257.4 (8)O2—Ti1—Ba1xii50.9 (10)
O2i—Ba1—O2ix90.60 (11)O1xii—Ti1—Ba1xii53.1 (3)
O2ii—Ba1—O2ix120.27 (12)Ba1—Ti1—Ba1xii71.17 (3)
O2iii—Ba1—O2ix176.2 (15)Ba1xi—Ti1—Ba1xii109.76 (3)
O2iv—Ba1—O2ix120.27 (12)Ba1xiii—Ti1—Ba1xii109.76 (3)
O1—Ba1—O2ix115.7 (10)Ba1xiv—Ti1—Ba1xii177.4 (6)
O1v—Ba1—O2ix58.3 (9)Ba1xv—Ti1—Ba1xii106.2 (6)
O1vi—Ba1—O2ix58.3 (9)Ti1—O1—Ti1iv180.000 (5)
O1vii—Ba1—O2ix115.7 (10)Ti1—O1—Ba193.5 (10)
O2viii—Ba1—O2ix85.6 (14)Ti1iv—O1—Ba186.5 (10)
O2—Ba1—O2ix57.4 (8)Ti1—O1—Ba1xiv93.5 (10)
O2i—Ba1—O2vii120.27 (12)Ti1iv—O1—Ba1xiv86.5 (10)
O2ii—Ba1—O2vii90.60 (11)Ba1—O1—Ba1xiv173 (2)
O2iii—Ba1—O2vii120.27 (12)Ti1—O1—Ba1xi93.5 (10)
O2iv—Ba1—O2vii176.2 (15)Ti1iv—O1—Ba1xi86.5 (10)
O1—Ba1—O2vii115.7 (10)Ba1—O1—Ba1xi89.78 (13)
O1v—Ba1—O2vii58.3 (9)Ba1xiv—O1—Ba1xi89.78 (13)
O1vi—Ba1—O2vii115.7 (10)Ti1—O1—Ba1xiii93.5 (10)
O1vii—Ba1—O2vii58.3 (9)Ti1iv—O1—Ba1xiii86.5 (10)
O2viii—Ba1—O2vii57.4 (8)Ba1—O1—Ba1xiii89.78 (13)
O2—Ba1—O2vii85.6 (14)Ba1xiv—O1—Ba1xiii89.78 (13)
O2ix—Ba1—O2vii57.4 (8)Ba1xi—O1—Ba1xiii173 (2)
O1—Ti1—O2x96.6 (15)Ti1vi—O2—Ti1167 (3)
O1—Ti1—O2xi96.6 (15)Ti1vi—O2—Ba1xvi94.5 (10)
O2x—Ti1—O2xi89.2 (3)Ti1—O2—Ba1xvi94.5 (10)
O1—Ti1—O2viii96.6 (15)Ti1vi—O2—Ba1xii94.5 (10)
O2x—Ti1—O2viii167 (3)Ti1—O2—Ba1xii94.5 (10)
O2xi—Ti1—O2viii89.2 (3)Ba1xvi—O2—Ba1xii93.2 (16)
O1—Ti1—O296.6 (15)Ti1vi—O2—Ba185.2 (11)
O2x—Ti1—O289.2 (3)Ti1—O2—Ba185.2 (11)
O2xi—Ti1—O2167 (3)Ba1xvi—O2—Ba1176.2 (15)
O2viii—Ti1—O289.2 (4)Ba1xii—O2—Ba190.60 (11)
O1—Ti1—O1xii180.000 (14)Ti1vi—O2—Ba1xiii85.2 (11)
O2x—Ti1—O1xii83.4 (15)Ti1—O2—Ba1xiii85.2 (11)
O2xi—Ti1—O1xii83.4 (15)Ba1xvi—O2—Ba1xiii90.60 (11)
O2viii—Ti1—O1xii83.4 (15)Ba1xii—O2—Ba1xiii176.2 (15)
O2—Ti1—O1xii83.4 (15)Ba1—O2—Ba1xiii85.6 (14)
O2i—Ba1—Ti1—O161.5 (15)O2xi—Ti1—O1—Ba1xiii135.0
O2ii—Ba1—Ti1—O161.5 (15)O2viii—Ti1—O1—Ba1xiii135.000 (3)
O2iii—Ba1—Ti1—O130.9 (5)O2—Ti1—O1—Ba1xiii45.000 (1)
O2iv—Ba1—Ti1—O130.9 (5)O1xii—Ti1—O1—Ba1xiii132 (100)
O1v—Ba1—Ti1—O1180.000 (3)Ba1—Ti1—O1—Ba1xiii90.0
O1vi—Ba1—Ti1—O192.9 (9)Ba1xi—Ti1—O1—Ba1xiii180.0
O1vii—Ba1—Ti1—O192.9 (8)Ba1xiv—Ti1—O1—Ba1xiii90.000 (3)
O2viii—Ba1—Ti1—O1124.9 (12)Ba1xv—Ti1—O1—Ba1xiii90.000 (1)
O2—Ba1—Ti1—O1124.9 (12)Ba1xii—Ti1—O1—Ba1xiii90.000 (2)
O2ix—Ba1—Ti1—O1151.3 (4)O2i—Ba1—O1—Ti1141.9 (10)
O2vii—Ba1—Ti1—O1151.3 (4)O2ii—Ba1—O1—Ti1141.9 (10)
O2i—Ba1—Ti1—O2x5.3 (12)O2iii—Ba1—O1—Ti1144.4 (8)
O2ii—Ba1—Ti1—O2x128 (3)O2iv—Ba1—O1—Ti1144.4 (8)
O2iii—Ba1—Ti1—O2x98 (2)O1v—Ba1—O1—Ti10.000 (10)
O2iv—Ba1—Ti1—O2x35.9 (12)O1vi—Ba1—O1—Ti186.5 (10)
O1—Ba1—Ti1—O2x66.9 (15)O1vii—Ba1—O1—Ti186.5 (10)
O1v—Ba1—Ti1—O2x113.1 (15)O2viii—Ba1—O1—Ti134.4 (7)
O1vi—Ba1—Ti1—O2x26.1 (17)O2—Ba1—O1—Ti134.4 (7)
O1vii—Ba1—Ti1—O2x159.8 (18)O2ix—Ba1—O1—Ti132.2 (7)
O2viii—Ba1—Ti1—O2x168 (3)O2vii—Ba1—O1—Ti132.2 (7)
O2—Ba1—Ti1—O2x58.1 (5)O2i—Ba1—O1—Ti1iv38.1 (10)
O2ix—Ba1—Ti1—O2x84.4 (12)O2ii—Ba1—O1—Ti1iv38.1 (10)
O2vii—Ba1—Ti1—O2x141.9 (19)O2iii—Ba1—O1—Ti1iv35.6 (8)
O2i—Ba1—Ti1—O2xi128 (3)O2iv—Ba1—O1—Ti1iv35.6 (8)
O2ii—Ba1—Ti1—O2xi5.3 (12)O1v—Ba1—O1—Ti1iv180.000 (10)
O2iii—Ba1—Ti1—O2xi35.9 (11)O1vi—Ba1—O1—Ti1iv93.5 (10)
O2iv—Ba1—Ti1—O2xi98 (2)O1vii—Ba1—O1—Ti1iv93.5 (10)
O1—Ba1—Ti1—O2xi66.9 (15)O2viii—Ba1—O1—Ti1iv145.6 (7)
O1v—Ba1—Ti1—O2xi113.1 (15)O2—Ba1—O1—Ti1iv145.6 (7)
O1vi—Ba1—Ti1—O2xi159.8 (18)O2ix—Ba1—O1—Ti1iv147.8 (7)
O1vii—Ba1—Ti1—O2xi26.1 (17)O2vii—Ba1—O1—Ti1iv147.8 (7)
O2viii—Ba1—Ti1—O2xi58.1 (5)O2i—Ba1—O1—Ba1xiv38.1 (10)
O2—Ba1—Ti1—O2xi168 (3)O2ii—Ba1—O1—Ba1xiv38.1 (10)
O2ix—Ba1—Ti1—O2xi141.9 (19)O2iii—Ba1—O1—Ba1xiv35.6 (8)
O2vii—Ba1—Ti1—O2xi84.4 (12)O2iv—Ba1—O1—Ba1xiv35.6 (8)
O2i—Ba1—Ti1—O2viii174 (3)O1v—Ba1—O1—Ba1xiv180.000 (10)
O2ii—Ba1—Ti1—O2viii63.4 (8)O1vi—Ba1—O1—Ba1xiv93.5 (10)
O2iii—Ba1—Ti1—O2viii94.0 (7)O1vii—Ba1—O1—Ba1xiv93.5 (10)
O2iv—Ba1—Ti1—O2viii155.9 (16)O2viii—Ba1—O1—Ba1xiv145.6 (7)
O1—Ba1—Ti1—O2viii124.9 (12)O2—Ba1—O1—Ba1xiv145.6 (7)
O1v—Ba1—Ti1—O2viii55.1 (12)O2ix—Ba1—O1—Ba1xiv147.8 (7)
O1vi—Ba1—Ti1—O2viii142.1 (15)O2vii—Ba1—O1—Ba1xiv147.8 (7)
O1vii—Ba1—Ti1—O2viii32.0 (14)O2i—Ba1—O1—Ba1xi124.6 (10)
O2—Ba1—Ti1—O2viii110 (2)O2ii—Ba1—O1—Ba1xi48.3 (18)
O2ix—Ba1—Ti1—O2viii83.8 (16)O2iii—Ba1—O1—Ba1xi50.9 (11)
O2vii—Ba1—Ti1—O2viii26.3 (8)O2iv—Ba1—O1—Ba1xi122.1 (14)
O2i—Ba1—Ti1—O263.4 (8)O1v—Ba1—O1—Ba1xi93.5 (10)
O2ii—Ba1—Ti1—O2174 (3)O1vi—Ba1—O1—Ba1xi180.0
O2iii—Ba1—Ti1—O2155.9 (16)O1vii—Ba1—O1—Ba1xi7 (2)
O2iv—Ba1—Ti1—O294.0 (7)O2viii—Ba1—O1—Ba1xi59.2 (10)
O1—Ba1—Ti1—O2124.9 (12)O2—Ba1—O1—Ba1xi127.9 (15)
O1v—Ba1—Ti1—O255.1 (12)O2ix—Ba1—O1—Ba1xi125.8 (9)
O1vi—Ba1—Ti1—O232.0 (14)O2vii—Ba1—O1—Ba1xi61.3 (15)
O1vii—Ba1—Ti1—O2142.1 (15)O2i—Ba1—O1—Ba1xiii48.3 (18)
O2viii—Ba1—Ti1—O2110 (2)O2ii—Ba1—O1—Ba1xiii124.6 (10)
O2ix—Ba1—Ti1—O226.3 (8)O2iii—Ba1—O1—Ba1xiii122.1 (14)
O2vii—Ba1—Ti1—O283.8 (16)O2iv—Ba1—O1—Ba1xiii50.9 (11)
O2i—Ba1—Ti1—O1xii118.5 (15)O1v—Ba1—O1—Ba1xiii93.5 (10)
O2ii—Ba1—Ti1—O1xii118.5 (15)O1vi—Ba1—O1—Ba1xiii7 (2)
O2iii—Ba1—Ti1—O1xii149.1 (5)O1vii—Ba1—O1—Ba1xiii180.0
O2iv—Ba1—Ti1—O1xii149.1 (5)O2viii—Ba1—O1—Ba1xiii127.9 (15)
O1—Ba1—Ti1—O1xii180.000 (2)O2—Ba1—O1—Ba1xiii59.2 (10)
O1v—Ba1—Ti1—O1xii0.000 (2)O2ix—Ba1—O1—Ba1xiii61.3 (15)
O1vi—Ba1—Ti1—O1xii87.1 (8)O2vii—Ba1—O1—Ba1xiii125.8 (9)
O1vii—Ba1—Ti1—O1xii87.1 (9)O1—Ti1—O2—Ti1vi0.000 (16)
O2viii—Ba1—Ti1—O1xii55.1 (12)O2x—Ti1—O2—Ti1vi96.6 (14)
O2—Ba1—Ti1—O1xii55.1 (12)O2xi—Ti1—O2—Ti1vi180.000 (2)
O2ix—Ba1—Ti1—O1xii28.7 (4)O2viii—Ti1—O2—Ti1vi96.6 (14)
O2vii—Ba1—Ti1—O1xii28.7 (4)O1xii—Ti1—O2—Ti1vi180.000 (14)
O2i—Ba1—Ti1—Ba1xi122.1 (15)Ba1—Ti1—O2—Ti1vi43.0 (6)
O2ii—Ba1—Ti1—Ba1xi0.9 (16)Ba1xi—Ti1—O2—Ti1vi49.9 (11)
O2iii—Ba1—Ti1—Ba1xi29.7 (6)Ba1xiii—Ti1—O2—Ti1vi43.0 (6)
O2iv—Ba1—Ti1—Ba1xi91.6 (5)Ba1xiv—Ti1—O2—Ti1vi49.9 (11)
O1—Ba1—Ti1—Ba1xi60.62 (19)Ba1xv—Ti1—O2—Ti1vi139.5 (6)
O1v—Ba1—Ti1—Ba1xi119.38 (19)Ba1xii—Ti1—O2—Ti1vi133.2 (9)
O1vi—Ba1—Ti1—Ba1xi153.5 (9)O1—Ti1—O2—Ba1xvi133.2 (9)
O1vii—Ba1—Ti1—Ba1xi32.3 (9)O2x—Ti1—O2—Ba1xvi37 (2)
O2viii—Ba1—Ti1—Ba1xi64.3 (12)O2xi—Ti1—O2—Ba1xvi46.8 (9)
O2—Ba1—Ti1—Ba1xi174.4 (12)O2viii—Ti1—O2—Ba1xvi130.2 (7)
O2ix—Ba1—Ti1—Ba1xi148.1 (4)O1xii—Ti1—O2—Ba1xvi46.8 (9)
O2vii—Ba1—Ti1—Ba1xi90.7 (5)Ba1—Ti1—O2—Ba1xvi176.2 (15)
O2i—Ba1—Ti1—Ba1xiii0.9 (16)Ba1xi—Ti1—O2—Ba1xvi176.9 (7)
O2ii—Ba1—Ti1—Ba1xiii122.1 (15)Ba1xiii—Ti1—O2—Ba1xvi90.2 (3)
O2iii—Ba1—Ti1—Ba1xiii91.6 (5)Ba1xiv—Ti1—O2—Ba1xvi83.3 (18)
O2iv—Ba1—Ti1—Ba1xiii29.7 (6)Ba1xv—Ti1—O2—Ba1xvi6.3 (14)
O1—Ba1—Ti1—Ba1xiii60.62 (19)Ba1xii—Ti1—O2—Ba1xvi93.6 (18)
O1v—Ba1—Ti1—Ba1xiii119.38 (19)O1—Ti1—O2—Ba1xii133.2 (9)
O1vi—Ba1—Ti1—Ba1xiii32.3 (9)O2x—Ti1—O2—Ba1xii130.2 (7)
O1vii—Ba1—Ti1—Ba1xiii153.5 (9)O2xi—Ti1—O2—Ba1xii46.8 (9)
O2viii—Ba1—Ti1—Ba1xiii174.4 (12)O2viii—Ti1—O2—Ba1xii37 (2)
O2—Ba1—Ti1—Ba1xiii64.3 (12)O1xii—Ti1—O2—Ba1xii46.8 (9)
O2ix—Ba1—Ti1—Ba1xiii90.7 (5)Ba1—Ti1—O2—Ba1xii90.2 (3)
O2vii—Ba1—Ti1—Ba1xiii148.1 (4)Ba1xi—Ti1—O2—Ba1xii83.3 (18)
O2i—Ba1—Ti1—Ba1xiv61.5 (15)Ba1xiii—Ti1—O2—Ba1xii176.2 (15)
O2ii—Ba1—Ti1—Ba1xiv61.5 (15)Ba1xiv—Ti1—O2—Ba1xii176.9 (7)
O2iii—Ba1—Ti1—Ba1xiv30.9 (5)Ba1xv—Ti1—O2—Ba1xii87.3 (6)
O2iv—Ba1—Ti1—Ba1xiv30.9 (5)O1—Ti1—O2—Ba143.0 (6)
O1—Ba1—Ti1—Ba1xiv0.000 (1)O2x—Ti1—O2—Ba1139.6 (9)
O1v—Ba1—Ti1—Ba1xiv180.0O2xi—Ti1—O2—Ba1137.0 (6)
O1vi—Ba1—Ti1—Ba1xiv92.9 (9)O2viii—Ti1—O2—Ba154 (2)
O1vii—Ba1—Ti1—Ba1xiv92.9 (9)O1xii—Ti1—O2—Ba1137.0 (6)
O2viii—Ba1—Ti1—Ba1xiv124.9 (12)Ba1xi—Ti1—O2—Ba16.9 (16)
O2—Ba1—Ti1—Ba1xiv124.9 (12)Ba1xiii—Ti1—O2—Ba186.0 (13)
O2ix—Ba1—Ti1—Ba1xiv151.3 (4)Ba1xiv—Ti1—O2—Ba192.9 (8)
O2vii—Ba1—Ti1—Ba1xiv151.3 (4)Ba1xv—Ti1—O2—Ba1177.5 (5)
O2i—Ba1—Ti1—Ba1xv118.5 (15)Ba1xii—Ti1—O2—Ba190.2 (3)
O2ii—Ba1—Ti1—Ba1xv118.5 (15)O1—Ti1—O2—Ba1xiii43.0 (6)
O2iii—Ba1—Ti1—Ba1xv149.1 (5)O2x—Ti1—O2—Ba1xiii54 (2)
O2iv—Ba1—Ti1—Ba1xv149.1 (5)O2xi—Ti1—O2—Ba1xiii137.0 (6)
O1—Ba1—Ti1—Ba1xv180.0O2viii—Ti1—O2—Ba1xiii139.6 (9)
O1v—Ba1—Ti1—Ba1xv0.0O1xii—Ti1—O2—Ba1xiii137.0 (6)
O1vi—Ba1—Ti1—Ba1xv87.1 (9)Ba1—Ti1—O2—Ba1xiii86.0 (13)
O1vii—Ba1—Ti1—Ba1xv87.1 (9)Ba1xi—Ti1—O2—Ba1xiii92.9 (8)
O2viii—Ba1—Ti1—Ba1xv55.1 (12)Ba1xiv—Ti1—O2—Ba1xiii6.9 (16)
O2—Ba1—Ti1—Ba1xv55.1 (12)Ba1xv—Ti1—O2—Ba1xiii96.5 (12)
O2ix—Ba1—Ti1—Ba1xv28.7 (4)Ba1xii—Ti1—O2—Ba1xiii176.2 (15)
O2vii—Ba1—Ti1—Ba1xv28.7 (4)O2i—Ba1—O2—Ti1vi28 (2)
O2i—Ba1—Ti1—Ba1xii118.5 (15)O2ii—Ba1—O2—Ti1vi94.5 (10)
O2ii—Ba1—Ti1—Ba1xii118.5 (15)O2iii—Ba1—O2—Ti1vi142.8 (5)
O2iii—Ba1—Ti1—Ba1xii149.1 (5)O2iv—Ba1—O2—Ti1vi85.5 (10)
O2iv—Ba1—Ti1—Ba1xii149.1 (5)O1—Ba1—O2—Ti1vi141.5 (14)
O1—Ba1—Ti1—Ba1xii180.0O1v—Ba1—O2—Ti1vi42.9 (14)
O1v—Ba1—Ti1—Ba1xii0.0O1vi—Ba1—O2—Ti1vi29.5 (10)
O1vi—Ba1—Ti1—Ba1xii87.1 (9)O1vii—Ba1—O2—Ti1vi146.1 (9)
O1vii—Ba1—Ti1—Ba1xii87.1 (9)O2viii—Ba1—O2—Ti1vi148.2 (7)
O2viii—Ba1—Ti1—Ba1xii55.1 (12)O2ix—Ba1—O2—Ti1vi40.8 (13)
O2—Ba1—Ti1—Ba1xii55.1 (12)O2vii—Ba1—O2—Ti1vi94.5 (10)
O2ix—Ba1—Ti1—Ba1xii28.7 (4)O2i—Ba1—O2—Ti1142.8 (5)
O2vii—Ba1—Ti1—Ba1xii28.7 (4)O2ii—Ba1—O2—Ti194.5 (10)
O2x—Ti1—O1—Ti1iv56 (100)O2iii—Ba1—O2—Ti128 (2)
O2xi—Ti1—O1—Ti1iv146 (100)O2iv—Ba1—O2—Ti185.5 (10)
O2viii—Ti1—O1—Ti1iv124 (100)O1—Ba1—O2—Ti129.5 (10)
O2—Ti1—O1—Ti1iv34 (100)O1v—Ba1—O2—Ti1146.1 (9)
O1xii—Ti1—O1—Ti1iv0.0O1vi—Ba1—O2—Ti1141.5 (14)
Ba1—Ti1—O1—Ti1iv79 (100)O1vii—Ba1—O2—Ti142.9 (14)
Ba1xi—Ti1—O1—Ti1iv169 (100)O2viii—Ba1—O2—Ti140.8 (13)
Ba1xiii—Ti1—O1—Ti1iv11 (100)O2ix—Ba1—O2—Ti1148.2 (7)
Ba1xiv—Ti1—O1—Ti1iv101 (100)O2vii—Ba1—O2—Ti194.5 (10)
Ba1xv—Ti1—O1—Ti1iv101 (100)O2i—Ba1—O2—Ba1xvi57.3 (11)
Ba1xii—Ti1—O1—Ti1iv79 (100)O2ii—Ba1—O2—Ba1xvi180.00 (6)
O2x—Ti1—O1—Ba1135.000 (4)O2iii—Ba1—O2—Ba1xvi57.3 (11)
O2xi—Ti1—O1—Ba1135.000 (1)O2iv—Ba1—O2—Ba1xvi0.0
O2viii—Ti1—O1—Ba145.000 (3)O1—Ba1—O2—Ba1xvi56.0 (7)
O2—Ti1—O1—Ba145.000 (1)O1v—Ba1—O2—Ba1xvi128.4 (7)
O1xii—Ti1—O1—Ba1138 (100)O1vi—Ba1—O2—Ba1xvi56.0 (7)
Ba1xi—Ti1—O1—Ba190.0O1vii—Ba1—O2—Ba1xvi128.4 (7)
Ba1xiii—Ti1—O1—Ba190.000 (3)O2viii—Ba1—O2—Ba1xvi126.3 (3)
Ba1xiv—Ti1—O1—Ba1180.000 (3)O2ix—Ba1—O2—Ba1xvi126.3 (3)
Ba1xv—Ti1—O1—Ba1180.0O2vii—Ba1—O2—Ba1xvi180.0
Ba1xii—Ti1—O1—Ba10.000 (3)O2i—Ba1—O2—Ba1xii122.7 (11)
O2x—Ti1—O1—Ba1xiv45.000 (4)O2ii—Ba1—O2—Ba1xii0.00 (6)
O2xi—Ti1—O1—Ba1xiv45.000 (1)O2iii—Ba1—O2—Ba1xii122.7 (11)
O2viii—Ti1—O1—Ba1xiv135.000 (3)O2iv—Ba1—O2—Ba1xii180.0
O2—Ti1—O1—Ba1xiv135.000 (1)O1—Ba1—O2—Ba1xii124.0 (7)
O1xii—Ti1—O1—Ba1xiv42 (100)O1v—Ba1—O2—Ba1xii51.6 (7)
Ba1—Ti1—O1—Ba1xiv180.0O1vi—Ba1—O2—Ba1xii124.0 (7)
Ba1xi—Ti1—O1—Ba1xiv90.0O1vii—Ba1—O2—Ba1xii51.6 (7)
Ba1xiii—Ti1—O1—Ba1xiv90.000 (3)O2viii—Ba1—O2—Ba1xii53.7 (3)
Ba1xv—Ti1—O1—Ba1xiv0.000 (1)O2ix—Ba1—O2—Ba1xii53.7 (3)
Ba1xii—Ti1—O1—Ba1xiv180.000 (2)O2vii—Ba1—O2—Ba1xii0.0
O2x—Ti1—O1—Ba1xi135.000 (4)O2i—Ba1—O2—Ba1xiii57.3 (11)
O2xi—Ti1—O1—Ba1xi45.000 (1)O2ii—Ba1—O2—Ba1xiii180.00 (6)
O2viii—Ti1—O1—Ba1xi45.000 (3)O2iii—Ba1—O2—Ba1xiii57.3 (11)
O2—Ti1—O1—Ba1xi135.000 (2)O2iv—Ba1—O2—Ba1xiii0.0
O1xii—Ti1—O1—Ba1xi48 (100)O1—Ba1—O2—Ba1xiii56.0 (7)
Ba1—Ti1—O1—Ba1xi90.0O1v—Ba1—O2—Ba1xiii128.4 (7)
Ba1xiii—Ti1—O1—Ba1xi180.000 (3)O1vi—Ba1—O2—Ba1xiii56.0 (7)
Ba1xiv—Ti1—O1—Ba1xi90.000 (3)O1vii—Ba1—O2—Ba1xiii128.4 (7)
Ba1xv—Ti1—O1—Ba1xi90.0O2viii—Ba1—O2—Ba1xiii126.3 (3)
Ba1xii—Ti1—O1—Ba1xi90.000 (3)O2ix—Ba1—O2—Ba1xiii126.3 (3)
O2x—Ti1—O1—Ba1xiii45.000 (4)O2vii—Ba1—O2—Ba1xiii180.0
Symmetry codes: (i) y, x, z1; (ii) x, y1, z1; (iii) y+1, x, z1; (iv) x, y, z1; (v) x1, y1, z; (vi) x1, y, z; (vii) x, y1, z; (viii) y+1, x, z; (ix) y, x, z; (x) y+1, x+1, z; (xi) x+1, y, z; (xii) x, y, z+1; (xiii) x, y+1, z; (xiv) x+1, y+1, z; (xv) x+1, y+1, z+1; (xvi) x, y+1, z+1.

Experimental details

Crystal data
Chemical formulaBaO3Ti
Mr233.24
Crystal system, space groupTetragonal, P4mm
Temperature (K)300
a, c (Å)3.9905 (13), 4.0412 (14)
V3)64.35 (4)
Z1
Radiation typeSynchrotron, λ = 0.83351 Å
µ (mm1)18.04
Crystal size (mm)0.0006 × 0.0006 × 0.0003
Data collection
DiffractometerRigaku Saturn 724
diffractometer
Absorption correction
No. of measured, independent and
observed [I > 2σ(I)] reflections
468, 88, 85
Rint0.094
(sin θ/λ)max1)0.586
Refinement
R[F2 > 2σ(F2)], wR(F2), S 0.052, 0.102, 1.17
No. of reflections88
No. of parameters9
Δρmax, Δρmin (e Å3)2.08, 1.98
Absolute structureFlack H D (1983), Acta Cryst. A39, 876-881
Absolute structure parameter0.8 (7)

Computer programs: Rapid Auto(Rigaku), SHELXS97 (Sheldrick, 1990), SHELXL97 (Sheldrick, 1997).

 

Footnotes

1Supplementary data for this paper are available from the IUCr electronic archives (Reference: IA5038 ). Services for accessing these data are described at the back of the journal.

Acknowledgements

We thank all the members of the X-ray pinpoint structure measurement group for their helpful discussions. We also thank Professor Satoshi Wada for the BaTiO3 sample preparation, and Professor Shinji Matsui and Mr Makoto Okada for the SEM measurement. Part of this research was supported by a Grant-in-Aid for Young Scientists (B) (No. 18750023) from the Japanese Ministry of Education, Culture, Sports, Science and Technology. This work was conducted at the BL40XU of SPring-8 with the approval of the Japan Synchrotron Radiation Research Institute (Proposal Nos. 2005A0885-S3-np, 2005B0930, 2006A1746, 2006B1726, 2007A1864 and 2007B1876).

References

First citationAoyagi, S., Kuroiwa, Y., Sawada, A., Yamashita, I. & Atake, T. (2002). J. Phys. Soc. Jpn, 71, 1218–1221.  Web of Science CrossRef CAS Google Scholar
First citationDavid, W. I. F. & Shankland, K. (2008). Acta Cryst. A64, 52–64.  Web of Science CrossRef CAS IUCr Journals Google Scholar
First citationDavid, W. I. F., Shankland, K., McCusker, L. B. & Baerlocher, Ch. (2002). Editors. Structure Determination from Powder Diffraction Data, pp. 1–11. Oxford University Press.  Google Scholar
First citationFukuyama, Y., Yasuda, N., Kim, J. E., Murayama, H., Ohshima, T., Tanaka, Y., Kimura, S., Kamioka, H., Moritomo, Y., Toriumi, K, Tanaka, H., Kato, K., Ishikawa, T. & Takata, M. (2008a). Rev. Sci. Instrum. 79, 045107.  Web of Science CrossRef PubMed Google Scholar
First citationFukuyama, Y., Yasuda, N., Kim, J. E., Murayama, H., Tanaka, Y., Kimura, S., Kato, K., Kohara, S., Moritomo, Y., Matsunaga, T., Kojima, R., Yamada, N., Tanaka, H., Ohshima, T. & Takata, M. (2008b). Appl. Phys. Express, 1, 045001.  Web of Science CrossRef Google Scholar
First citationInoue, K., Oka, T., Suzuki, T., Yagi, N., Takeshita, K., Goto, S. & Ishikawa, T. (2001). Nucl. Instrum. Methods Phys. Res. A, 467468, 674–677.  Web of Science CrossRef CAS Google Scholar
First citationKimura, S., Moritomo, Y., Tanaka, Y., Tanaka, H., Toriumi, K., Kato, K., Yasuda, N., Fukuyama, Y., Kim, J. E., Murayama, H. & Takata, M. (2007). AIP Conf. Proc. 879, 1238–1241.  CrossRef CAS Google Scholar
First citationOhsumi, K., Hagiya, K. & Ohmasa, M. (1991). J. Appl. Cryst. 24, 340–348.  CrossRef CAS Web of Science IUCr Journals Google Scholar
First citationOzawa, A., Tamamura, T., Ishii, T., Yoshihara, H. & Kagoshima, Y. (1997). Microelectron. Eng. 35, 525–529.  CrossRef CAS Web of Science Google Scholar
First citationRiekel, C., Burghammer, M. & Schertler, G. (2005). Curr. Opin. Struct. Biol. 15, 556–562.  Web of Science CrossRef PubMed CAS Google Scholar
First citationRigaku Corporation (1998). RAPID-AUTO. Rigaku Corporation, Tokyo, Japan.  Google Scholar
First citationSheldrick, G. M. (2008). Acta Cryst. A64, 112–122.  Web of Science CrossRef CAS IUCr Journals Google Scholar
First citationVolkringer, C., Popov, D., Loiseau, T., Guillou, N., Ferey, G., Haouas, M., Taulelle, F., Mellot-Draznieks, C., Burghammer, M. & Riekel, C. (2007). Nat. Mater. 6, 760–764.  Web of Science CrossRef PubMed CAS Google Scholar
First citationYashima, M., Hoshina, T., Ishimura, D., Kobayashi, S., Nakamura, W., Tsurumi, T. & Wada, S. (2005). J. Appl. Phys. 98, 014313.  Web of Science CrossRef Google Scholar

This is an open-access article distributed under the terms of the Creative Commons Attribution (CC-BY) Licence, which permits unrestricted use, distribution, and reproduction in any medium, provided the original authors and source are cited.

Journal logoJOURNAL OF
SYNCHROTRON
RADIATION
ISSN: 1600-5775
Volume 16| Part 3| May 2009| Pages 352-357
Follow J. Synchrotron Rad.
Sign up for e-alerts
Follow J. Synchrotron Rad. on Twitter
Follow us on facebook
Sign up for RSS feeds