Aluminium germanium lithium, AlGeLi, crystallizes in two cubic dimorphs. The structure of the F\overline{4}3m form, already inferred from powder data, has been confirmed by both powder and single-crystal X-ray diffraction studies. The second dimorph, not previously identified, adopts a disordered centrosymmetric structure with space group Fm\overline{3}m.

Supporting information

cif

Crystallographic Information File (CIF) https://doi.org/10.1107/S0108270105007171/fa1121sup1.cif
Contains datablocks I, global, II

hkl

Structure factor file (CIF format) https://doi.org/10.1107/S0108270105007171/fa1121Isup2.hkl
Contains datablock I

hkl

Structure factor file (CIF format) https://doi.org/10.1107/S0108270105007171/fa1121IIsup3.hkl
Contains datablock II

Comment top

So far the literature related to the ternary system Li–Al–Ge has been very poor. On the basis of X-ray powder diffraction, a cubic non-centrosymmetric structure has been proposed for LiAlGe, with either ordered or disordered atomic arrangements (Nowotny & Holub, 1960; Bockelman & Schuster, 1974; Schuster et al., 1976). In all cases, the structure was depicted with one among four 43m sites empty. Bockelman & Schuster (1974) refer to the cubic compound Li2AlGe (a = 6.163 Å) without giving any more structural details. We decided to synthesize the compounds LiAlGe and Li2AlGe in order to define precisely their crystal structures.

The alloy prepared with the 1:1:1 stoichiometry leads to a homogeneous product, for which the X-ray powder diffraction pattern was perfectly indexed in a cubic cell [a = 5.9913 (1) Å] and further refined by the Rietveld technique in space group F43m to good agreement factors (Rp = 7.66% and RBragg = 4.92%). Meanwhile, the structure and the absolute configuration [Flack (1983) parameter = −0.01 (4)] were determined from good quality intensity data (Rint = 3.96%) collected from a single-crystal [a = 5.9784 (9) Å] on a Nonius single-point detector diffractometer. The structure refinement was carried out to R(F) = 1.13% [inversion of the configuration leads to an R(F) of 5.85%]. Our results confirm the ordered and non-centrosymmetric atomic arrangement for the LiAlGe polymorph (I). The atomic arrangement along the body diagonal of the cubic cell is vacancy (0,0,0) – Al (1/4,1/4,1/4) – Ge (1/2,1/2,1/2) – Li (3/4,3/4,3/4).

All attempts to prepare Li2AlGe were unsuccessful. Starting from the 2:1:1 stoichiometry, we obtained a material that displayed a two-phase X-ray powder pattern with the main component indexed in a cubic cell with an a parameter of 6.1528 (2) Å. The minor component lines were indexed using the DICVOL program (Boultif & Louer, 1991) in an I-centered tetragonal cell (a = 3.842 Å and c = 8.544 Å). A single-crystal could be extracted from this mixture and diffracted intensities were recorded on an Xcalibur CCD diffractometer. The statistical tests from SHELXS97 gave a strong evidence for centrosymmetry. The structure was first solved and refined with a disordered atomic arrangement in the space group Fm3m [a = 6.1370 (8) Å and R(F) = 3.76%].

Attempts to refine the structure in the other cubic symmetries F43m, F432 (m3m Laue symmetry), Fm3 and F23 (m3 Laue symmetry) gave no improvement. Since in some cases twinning can simulate centrosymmetry, we submitted the data to the twinning test server (Yeates, 1997); there was no hint of merohedral (perfect or partial) twinning. Nevertheless, we have tested various combinations of merohedral (mirror plane or twofold axis) and inversion twinning without success. Finally, the best solution was obtained in the Fm3m centrosymmetric space group with Li/Al atomic mixing at site 4b. The refinement of LiAlGe polymorph (II) is in accordance with the Al/Ge and Al/Li ratios obtained from SEM–EDX (scanning electron microcopy/energy-dispersive X-ray diffraction) and AAA (in full?) analyses.

In the non-centrosymmetric ordered form (I), the Ge atom is tetrahedrally surrounded by four Al and four Li atoms at 2.5886 (4) Å. In the centrosymmetric disordered polymorph (II), four Al and four Li atoms are statistically arranged at 2.6574 (4) Å at the apices of a cube around the Ge atom. Such statistical disorder in the Ge neighborhood might be responsible for the expansion of the unit cell.

In order to quantify how much such disorder can modify the unit-cell parameters, we have performed plane-wave DFT (denisty functional theory) calculations in the GGA/PBE approximation using the program CASTEP (Payne et al., 1992) distributed inside the Accelrys (2002) commercial package. Ultrasoft pseudopotentials were used for all atoms. The atomic disorder in (II) was modeled with the 2 × 2 × 2 supercell that retains the Fm3m symmetry. Geometry was optimized in the supercell with Ge atoms at sites a (multiplicity 4), b (4) and d (24), and Li and Al atoms at f (32) (x, x, x with refined x = 0.6233 and 0.8705, respectively). The optimized unit-cell parameter of 6.0921 Å for the subcell only deviates by 0.73% from the experimental one (a = 6.1370 Å). Comparatively, the geometry optimization of the F43m unit cell of (I) gave 6.0264 Å instead of 5.9784 Å (experimental, 0.80% deviation). The calculated total energies indicate that the non-centrosymmetric polymorph (I) is more stable than the centrosymmetric polymorph (II). The hypothetical compound Li2AlGe obtained by the Li-filling of vacancies in the cubic LiAlGe structures would display a cell parameter of 6.252 Å (Fm3m) or 6.406 Å (F43m) (Tillard et al., 2005).

In conclusion, we can assert that the compound LiAlGe exists in two cubic forms. The Al/Li substitutional disorder at site 4a (Fm3m centrosymmetric structure) is responsible for the 0.16 Å increase in the cell parameter with respect of the ordered F43m structure.

Experimental top

Germanium powder (Strem chemicals, 99.999% pure) was used without purification; aluminium foil (Goodfellow, 99.999% pure, 0.5 mm) and lithium (ingot, Gogema, 99.94% pure, Mg free) were scraped to remove surface impurities. Alloys were prepared from the elements inside tantalum tubes, weld-sealed in argon atmosphere, and enclosed in stainless steel or silica jackets filled with argon to protect tantalum from oxidation at high temperatures. Mixtures of elements were heated to an appropriate temperature (about 1273 K) and kept at this temperature for several hours, during which they were shaken several times for good homogenization of the melts. The mixtures were then allowed to cool slowly to room temperature for crystal growth. Alloys were prepared at atomic ratios of 1:1:1 and 2:1:1 with the aim of obtaining the compounds LiAlGe and Li2AlGe previously cited in the literature. Crystals resulting from the two preparations were selected using a microscope inside a glove-box filled with purified argon. These crystals were inserted into thin-walled glass capillaries and then sealed to be used for checking singularity and crystal quality and for further X-ray investigations. The best diffracting single crystals were chosen for data collection at room temperature.

Computing details top

Data collection: CAD-4 Software (Enraf–Nonius, 1989) for (I); CrysAlis CCD (Oxford Diffraction, 2001) for (II). Cell refinement: CAD-4 Software for (I); CrysAlis RED (Oxford Diffraction, 2001) for (II). Data reduction: local program for (I); CrysAlis RED for (II). For both compounds, program(s) used to solve structure: SHELXS97 (Sheldrick, 1997); program(s) used to refine structure: SHELXL97 (Sheldrick, 1997). Molecular graphics: program (reference?) for (I); program (reference)? for (II). Software used to prepare material for publication: program (reference?) for (I); program (reference)? for (II).

Figures top
[Figure 1] Fig. 1. Representation of the cubic cell of the F43m LiAlGe polymorph (I).
[Figure 2] Fig. 2. Representation of the cubic cell of the Fm3 m LiAlGe polymorph (II).
(I) Lithium Aluminium Germanium top
Crystal data top
AlGeLiDx = 3.312 Mg m3
Mr = 106.51Mo Kα radiation, λ = 0.71070 Å
Cubic, F43mCell parameters from 25 reflections
Hall symbol: F -4 2 3θ = 5.9–20.9°
a = 5.9784 (9) ŵ = 14.25 mm1
V = 213.67 (6) Å3T = 293 K
Z = 4Platelet, metallic dark grey
F(000) = 1920.12 × 0.07 × 0.03 mm
Data collection top
Enraf–Nonius CAD-4
diffractometer
67 reflections with I > 2σ(I)
Radiation source: fine-focus sealed tubeRint = 0.040
Graphite monochromatorθmax = 34.5°, θmin = 5.9°
ω/θ scansh = 09
Absorption correction: numerical
(numerical type provided by SHELX76; Sheldrick, 1976)
k = 09
Tmin = 0.32, Tmax = 0.68l = 99
1083 measured reflections3 standard reflections every 100 reflections
67 independent reflections intensity decay: < 1%
Refinement top
Refinement on F2Secondary atom site location: difference Fourier map
Least-squares matrix: full w = 1/[σ2(Fo2) + (0.0094P)2 + 0.1227P]
where P = (Fo2 + 2Fc2)/3
R[F2 > 2σ(F2)] = 0.011(Δ/σ)max < 0.001
wR(F2) = 0.028Δρmax = 0.42 e Å3
S = 1.27Δρmin = 0.12 e Å3
67 reflectionsExtinction correction: SHELXL97, Fc*=kFc[1+0.001xFc2λ3/sin(2θ)]-1/4
6 parametersExtinction coefficient: 0.030 (4)
0 restraintsAbsolute structure: Flack (1983), 28 Friedel pairs?
Primary atom site location: structure-invariant direct methodsAbsolute structure parameter: 0.02 (4)
Crystal data top
AlGeLiZ = 4
Mr = 106.51Mo Kα radiation
Cubic, F43mµ = 14.25 mm1
a = 5.9784 (9) ÅT = 293 K
V = 213.67 (6) Å30.12 × 0.07 × 0.03 mm
Data collection top
Enraf–Nonius CAD-4
diffractometer
67 reflections with I > 2σ(I)
Absorption correction: numerical
(numerical type provided by SHELX76; Sheldrick, 1976)
Rint = 0.040
Tmin = 0.32, Tmax = 0.683 standard reflections every 100 reflections
1083 measured reflections intensity decay: < 1%
67 independent reflections
Refinement top
R[F2 > 2σ(F2)] = 0.0110 restraints
wR(F2) = 0.028Δρmax = 0.42 e Å3
S = 1.27Δρmin = 0.12 e Å3
67 reflectionsAbsolute structure: Flack (1983), 28 Friedel pairs?
6 parametersAbsolute structure parameter: 0.02 (4)
Special details top

Geometry. All e.s.d.'s (except the e.s.d. in the dihedral angle between two l.s. planes) are estimated using the full covariance matrix. The cell e.s.d.'s are taken into account individually in the estimation of e.s.d.'s in distances, angles and torsion angles; correlations between e.s.d.'s in cell parameters are only used when they are defined by crystal symmetry. An approximate (isotropic) treatment of cell e.s.d.'s is used for estimating e.s.d.'s involving l.s. planes.

Refinement. Refinement of F2 against ALL reflections. The weighted R-factor wR and goodness of fit S are based on F2, conventional R-factors R are based on F, with F set to zero for negative F2. The threshold expression of F2 > σ(F2) is used only for calculating R-factors(gt) etc. and is not relevant to the choice of reflections for refinement. R-factors based on F2 are statistically about twice as large as those based on F, and R- factors based on ALL data will be even larger.

Fractional atomic coordinates and isotropic or equivalent isotropic displacement parameters (Å2) top
xyzUiso*/Ueq
Ge0.50000.50000.50000.0063 (2)*
Li0.75000.75000.75000.016 (5)*
Al0.25000.75000.75000.0073 (6)*
Geometric parameters (Å, º) top
Ge—Ali2.5886 (4)Li—Al2.9890 (5)
Ge—Li2.5886 (4)
Ali—Ge—Alii109.5Ge—Li—Geiii109.5
Li—Ge—Lii109.5
Symmetry codes: (i) x, y1/2, z1/2; (ii) x+1/2, y1/2, z; (iii) x+1/2, y+1/2, z.
(II) top
Crystal data top
AlGeLiDx = 3.061 Mg m3
Mr = 106.51Mo Kα radiation, λ = 0.71073 Å
Cubic, Fm3mCell parameters from 1298 reflections
Hall symbol: -F 4 2 3θ = 5.8–34.6°
a = 6.1370 (8) ŵ = 13.17 mm1
V = 231.14 (5) Å3T = 293 K
Z = 4Triangle, metallic dark grey
F(000) = 1920.15 × 0.12 × 0.08 mm
Data collection top
Oxford Diffraction Xcalibur CCD
diffractometer
41 independent reflections
Radiation source: fine-focus sealed tube41 reflections with I > 2σ(I)
Graphite monochromatorRint = 0.071
ω scansθmax = 34.6°, θmin = 5.8°
Absorption correction: numerical
(CrysAlis RED; Oxford Diffraction, 2001; Clark & Reid, 1995)
h = 99
Tmin = 0.20, Tmax = 0.41k = 99
1298 measured reflectionsl = 99
Refinement top
Refinement on F2Primary atom site location: structure-invariant direct methods
Least-squares matrix: fullSecondary atom site location: difference Fourier map
R[F2 > 2σ(F2)] = 0.038 w = 1/[σ2(Fo2) + (0.0546P)2 + 2.038P]
where P = (Fo2 + 2Fc2)/3
wR(F2) = 0.090(Δ/σ)max < 0.001
S = 1.27Δρmax = 0.93 e Å3
41 reflectionsΔρmin = 0.72 e Å3
4 parametersExtinction correction: SHELXL97, Fc*=kFc[1+0.001xFc2λ3/sin(2θ)]-1/4
0 restraintsExtinction coefficient: 0.07 (2)
Crystal data top
AlGeLiZ = 4
Mr = 106.51Mo Kα radiation
Cubic, Fm3mµ = 13.17 mm1
a = 6.1370 (8) ÅT = 293 K
V = 231.14 (5) Å30.15 × 0.12 × 0.08 mm
Data collection top
Oxford Diffraction Xcalibur CCD
diffractometer
41 independent reflections
Absorption correction: numerical
(CrysAlis RED; Oxford Diffraction, 2001; Clark & Reid, 1995)
41 reflections with I > 2σ(I)
Tmin = 0.20, Tmax = 0.41Rint = 0.071
1298 measured reflections
Refinement top
R[F2 > 2σ(F2)] = 0.0384 parameters
wR(F2) = 0.0900 restraints
S = 1.27Δρmax = 0.93 e Å3
41 reflectionsΔρmin = 0.72 e Å3
Special details top

Geometry. All e.s.d.'s (except the e.s.d. in the dihedral angle between two l.s. planes) are estimated using the full covariance matrix. The cell e.s.d.'s are taken into account individually in the estimation of e.s.d.'s in distances, angles and torsion angles; correlations between e.s.d.'s in cell parameters are only used when they are defined by crystal symmetry. An approximate (isotropic) treatment of cell e.s.d.'s is used for estimating e.s.d.'s involving l.s. planes.

Refinement. Refinement of F2 against ALL reflections. The weighted R-factor wR and goodness of fit S are based on F2, conventional R-factors R are based on F, with F set to zero for negative F2. The threshold expression of F2 > σ(F2) is used only for calculating R-factors(gt) etc. and is not relevant to the choice of reflections for refinement. R-factors based on F2 are statistically about twice as large as those based on F, and R- factors based on ALL data will be even larger.

Fractional atomic coordinates and isotropic or equivalent isotropic displacement parameters (Å2) top
xyzUiso*/UeqOcc. (<1)
Ge0.00000.00000.00000.0231 (9)*
Li10.25000.25000.25000.0264 (13)*0.50
Al10.25000.25000.25000.0264 (13)*0.50
Geometric parameters (Å, º) top
Ge—Li1/Al12.6574 (4)Li1/Al1—Li1/Al1i3.0685 (5)
Al1ii—Ge—Al1iii109.5Li1—Ge—Li1iv109.5
Li1ii—Ge—Al1iii109.5
Symmetry codes: (i) x, y+1/2, z+1/2; (ii) x, y, z; (iii) x+1/2, y+1/2, z; (iv) x1/2, y1/2, z.

Experimental details

(I)(II)
Crystal data
Chemical formulaAlGeLiAlGeLi
Mr106.51106.51
Crystal system, space groupCubic, F43mCubic, Fm3m
Temperature (K)293293
a (Å)5.9784 (9) 6.1370 (8)
V3)213.67 (6)231.14 (5)
Z44
Radiation typeMo KαMo Kα
µ (mm1)14.2513.17
Crystal size (mm)0.12 × 0.07 × 0.030.15 × 0.12 × 0.08
Data collection
DiffractometerEnraf–Nonius CAD-4
diffractometer
Oxford Diffraction Xcalibur CCD
diffractometer
Absorption correctionNumerical
(numerical type provided by SHELX76; Sheldrick, 1976)
Numerical
(CrysAlis RED; Oxford Diffraction, 2001; Clark & Reid, 1995)
Tmin, Tmax0.32, 0.680.20, 0.41
No. of measured, independent and
observed [I > 2σ(I)] reflections
1083, 67, 67 1298, 41, 41
Rint0.0400.071
(sin θ/λ)max1)0.7980.798
Refinement
R[F2 > 2σ(F2)], wR(F2), S 0.011, 0.028, 1.27 0.038, 0.090, 1.27
No. of reflections6741
No. of parameters64
Δρmax, Δρmin (e Å3)0.42, 0.120.93, 0.72
Absolute structureFlack (1983), 28 Friedel pairs??
Absolute structure parameter0.02 (4)?

Computer programs: CAD-4 Software (Enraf–Nonius, 1989), CrysAlis CCD (Oxford Diffraction, 2001), CAD-4 Software, CrysAlis RED (Oxford Diffraction, 2001), local program, CrysAlis RED, SHELXS97 (Sheldrick, 1997), SHELXL97 (Sheldrick, 1997), program (reference?), program (reference)?.

Selected bond lengths (Å) for (I) top
Ge—Ali2.5886 (4)Li—Al2.9890 (5)
Ge—Li2.5886 (4)
Symmetry code: (i) x, y1/2, z1/2.
Selected bond lengths (Å) for (II) top
Ge—Li1/Al12.6574 (4)Li1/Al1—Li1/Al1i3.0685 (5)
Symmetry code: (i) x, y+1/2, z+1/2.
 

Subscribe to Acta Crystallographica Section C: Structural Chemistry

The full text of this article is available to subscribers to the journal.

If you have already registered and are using a computer listed in your registration details, please email support@iucr.org for assistance.

Buy online

You may purchase this article in PDF and/or HTML formats. For purchasers in the European Community who do not have a VAT number, VAT will be added at the local rate. Payments to the IUCr are handled by WorldPay, who will accept payment by credit card in several currencies. To purchase the article, please complete the form below (fields marked * are required), and then click on `Continue'.
E-mail address* 
Repeat e-mail address* 
(for error checking) 

Format*   PDF (US $40)
   HTML (US $40)
   PDF+HTML (US $50)
In order for VAT to be shown for your country javascript needs to be enabled.

VAT number 
(non-UK EC countries only) 
Country* 
 

Terms and conditions of use
Contact us

Follow Acta Cryst. C
Sign up for e-alerts
Follow Acta Cryst. on Twitter
Follow us on facebook
Sign up for RSS feeds