Acta Cryst. (2014). A70, C92
Download citation
link to html
Various Tsai-type quasicrystals and approximants have been synthesized by replacing the constituent elements of the Cd-RE systems, based on the condition, (e/a)~2.0,. However, systems containing transition metals (TMs) have been rarely reported and, therefore, in this work we aimed to synthesize TM-bearing Tsai-type quasicrystals and approximants. Starting from the composition of the Ga-Pd-Gd 1/1 approximant [1], a search of TM-bearing approximants was performed by replacing Pd (1.376 Å) by Pt (1.378 Å). In this research, alloys of various compositions around the reported composition of 1/1 Ga-Pd-Gd were prepared by arc melting and they were then annealed at various conditions. The phase constitution was studied by X-ray diffraction and the thermal stability of the phases was examined by differential thermal analysis (DTA) for samples before and after annealing. As a result, we have observed formation of both 1/1 and 2/1 approximants with a=14.37 Å and 23.23 Å, respectively. The DTA curve exhibits no exothermic peak in the heating run up to the melting point (Tm=1180 K) for the 2/1 approximant, which suggests that the obtained 2/1 approximant is thermally stable up to Tm. The magnetic properties of the 1/1 and 2/1 approximants will be reported in the presentation.

Follow Acta Cryst. A
Sign up for e-alerts
Follow Acta Cryst. on Twitter
Follow us on facebook
Sign up for RSS feeds