J. Appl. Cryst. (2001). 34, 196-202 [ doi:10.1107/S0021889801002485 ]
Abstract: A procedure for Rietveld quantitative amorphous content analysis (RQACA) is outlined, in which the effects of systematic errors in the powder patterns are studied. The method derives the amorphous content from the small overestimation of an internal crystalline standard in a Rietveld refinement of an appropriate mixture. Of several standards studied, Al2O3 gave the best results. The statistical analysis of standard mixtures with a known amount of amorphous content indicated that this is a precise and accurate tool. It enables the measurement of the amorphous content with an accuracy close to 1%. Sample preparation and Rietveld analysis need to be optimized in order to minimize the systematic errors. The analysis of samples with phases displaying strong preferred orientation effects gives very high errors in the amorphous content. Samples with different absorption coefficients have also been studied in order to evaluate the importance of microabsorption. This plays an important role but it can be adequately corrected if the absorption coefficients of the standard and the sample are not very different. RQACA has been applied to tricalcium silicate, C3S, which is the main component of Portland cement. The average amorphous content of C3S, after microabsorption correction using two standards of higher and lower absorption coefficients, was found to be 19%.
Keywords: Rietveld refinement; amorphous phase; cements.
Copyright © International Union of Crystallography
IUCr Webmaster